→Bendability
The measure for bendability of a strip material is the smallest possible bending radius r of a sample piece of given material thickness s without appearance of surface cracking. Bending tests are performed as either 90 degree bends according to ISO 7438 or as defined forth-and-back bending. The bendabilty of naturally hard copper alloys is significantly better perpendicular to the rolling direction than parallel to it [[#figures10|(Figs. 4 – 7)]]<!--(Figs. 5.41 and 5.42)-->.
<div class="multiple-images">
<figure id="fig:Smallest possible bend radii for 90 bends as function">
[[File:Smallest possible bend radii for 90 bends as function.jpg|right|thumb|Figure 4: Smallest possible bend radii for 90° bends as a function of the 0.2% yield strength R<sub>p0.2</sub> – bend line perpendicular to the rolling direction (Wieland)]]
</figure>
<figure id="fig:Smallest possible bend radii as a functionbend line parallel to the rolling direction">
[[File:Smallest possible bend radii as a functionbend line parallel to the rolling direction.jpg|right|thumb|Figure 5: Smallest possible bend radii for 90° bends as a function of the 0.2% yield strength R<sub>p0.2</sub> – bend line parallel to the rolling direction (Wieland)]]
</figure>
</div>