<xr id="fig:fig2Softening of Au after annealing for 0.95 hrs"/> Fig. 2.9: Softening of Au after annealing for 0.5 hrs after 80% cold working
<xr id="fig:fig2.10Strain hardening of AuPt10 by cold working"/> Fig. 2.10: Strain hardening of AuPt10 by cold working
<xr id="fig:fig2.11Strain hardening of AuAg20 by cold working"/> Fig. 2.11: Strain hardening of AuAg20 by cold working
<xr id="fig:fig2.12Strain hardening of AuAg30 by cold working"/> Fig. 2.12: Strain hardening of AuAg30 by cold working
<xr id="fig:fig2.13Strain hardening of AuNi5 by cold working"/> Fig. 2.13: Strain hardening of AuNi5 by cold working
<xr id="fig:fig2Softening of AuNi5 after annealing for 0.145 hrs"/> Fig. 2.14: Softening of AuNi5 after annealing for 0.5 hrs after 80% cold working
<xr id="fig:fig2.15Strain hardening of AuCo5 by cold working"/> Fig. 2.15: Strain hardening of AuCo5 by cold working
<xr id="fig:fig2.16Precipitation hardening of AuCo5 at"/> Fig. 2.16: Precipitation hardening of AuCo5 at 400°C hardening temperature
<xr id="fig:fig2.17Strain hardening of AuAg25Pt6 by cold working"/> Fig. 2.17: Strain hardening of AuAg25Pt6 by cold working
<xr id="fig:fig2.18Strain hardening of AuAg26Ni3 by cold working"/> Fig. 2.18: Strain hardening of AuAg26Ni3 by cold working
<xr id="fig:fig2Softening of AuAg26Ni3 after annealing for 0.195-hrs"/> Fig. 2.19: Softening of AuAg26Ni3 after annealing for 0.5 hrs after 80% cold working
<xr id="fig:fig2.20Strain hardening of AuAg25Cu5 by cold working"/> Fig. 2.20: Strain hardening of AuAg25Cu5 by cold working
<xr id="fig:fig2.21Strain hardening of AuAg20Cu10 by cold working"/> Fig. 2.21: Strain hardening of AuAg20Cu10 by cold working
<xr id="fig:fig2Softening of AuAg20Cu10 after annealing for 0.225 hrs"/> Fig. 2.22: Softening of AuAg20Cu10 after annealing for 0.5 hrs after 80% cold working
<xr id="fig:fig2.23Strain hardening of AuCu14Pt9Ag4 by cold working"/> Fig. 2.23: Strain hardening of AuCu14Pt9Ag4 by cold working
<xr id="fig:fig2.24Precipitation hardening of AuCu14Pt9Ag4"/> Fig. 2.24: Precipitation hardening of AuCu14Pt9Ag4 at different hardening temperatures after 50% cold working
</figure>
<figure id="fig:fig2Softening of Au after annealing for 0.95 hrs">
[[File:Softening of Au after annealing for 0.5 hrs.jpg|left|thumb|<caption>Softening of Au after annealing for 0.5 hrs after 80% cold working</caption>]]
</figure>
<figure id="fig:fig2.10Strain hardening of AuPt10 by cold working">
[[File:Strain hardening of AuPt10 by cold working.jpg|left|thumb|<caption>Strain hardening of AuPt10 by cold working</caption>]]
</figure>
<figure id="fig:fig2.11Strain hardening of AuAg20 by cold working">
[[File:Strain hardening of AuAg20 by cold working.jpg|left|thumb|<caption>Strain hardening of AuAg20 by cold working</caption>]]
</figure>
<figure id="fig:fig2.12Strain hardening of AuAg30 by cold working">
[[File:Strain hardening of AuAg30 by cold working.jpg|left|thumb|<caption>Strain hardening of AuAg30 by cold working</caption>]]
</figure>
<figure id="fig:fig2.13Strain hardening of AuNi5 by cold working">
[[File:Strain hardening of AuNi5 by cold working.jpg|left|thumb|<caption>Strain hardening of AuNi5 by cold working</caption>]]
</figure>
<figure id="fig:fig2Softening of AuNi5 after annealing for 0.145 hrs">
[[File:Softening of AuNi5 after annealing for 0.5 hrs.jpg|left|thumb|<caption>Softening of AuNi5 after annealing for 0.5 hrs after 80% cold working</caption>]]
</figure>
<figure id="fig:fig2.15Strain hardening of AuCo5 by cold working">
[[File:Strain hardening of AuCo5 by cold working.jpg|left|thumb|<caption>Strain hardening of AuCo5 by cold working</caption>]]
</figure>
<figure id="fig:fig2.16Precipitation hardening of AuCo5 at">
[[File:Precipitation hardening of AuCo5 at.jpg|left|thumb|<caption>Precipitation hardening of AuCo5 at 400°C hardening temperature</caption>]]
</figure>
<figure id="fig:fig2.17Strain hardening of AuAg25Pt6 by cold working">
[[File:Strain hardening of AuAg25Pt6 by cold working.jpg|left|thumb|<caption>Strain hardening of AuAg25Pt6 by cold working</caption>]]
</figure>
<figure id="fig:fig2.18Strain hardening of AuAg26Ni3 by cold working">
[[File:Strain hardening of AuAg26Ni3 by cold working.jpg|left|thumb|<caption>Strain hardening of AuAg26Ni3 by cold working</caption>]]
</figure>
<figure id="fig:fig2Softening of AuAg26Ni3 after annealing for 0.195-hrs">
[[File:Softening of AuAg26Ni3 after annealing for 0.5-hrs.jpg|left|thumb|<caption>Softening of AuAg26Ni3 after annealing for 0.5 hrs after 80% cold working</caption>]]
</figure>
<figure id="fig:fig2.20Strain hardening of AuAg25Cu5 by cold working">
[[File:Strain hardening of AuAg25Cu5 by cold working.jpg|left|thumb|<caption>Strain hardening of AuAg25Cu5 by cold working</caption>]]
</figure>
<figure id="fig:fig2.21Strain hardening of AuAg20Cu10 by cold working">
[[File:Strain hardening of AuAg20Cu10 by cold working.jpg|left|thumb|<caption>Strain hardening of AuAg20Cu10 by cold working</caption>]]
</figure>
<figure id="fig:fig2Softening of AuAg20Cu10 after annealing for 0.225 hrs">
[[File:Softening of AuAg20Cu10 after annealing for 0.5 hrs.jpg|left|thumb|<caption>Softening of AuAg20Cu10 after annealing for 0.5 hrs after 80% cold working</caption>]]
</figure>
<figure id="fig:fig2.23Strain hardening of AuCu14Pt9Ag4 by cold working">
[[File:Strain hardening of AuCu14Pt9Ag4 by cold working.jpg|left|thumb|<caption>Strain hardening of AuCu14Pt9Ag4 by cold working</caption>]]
</figure>
<figure id="fig:fig2.24Precipitation hardening of AuCu14Pt9Ag4">
[[File:Precipitation hardening of AuCu14Pt9Ag4.jpg|left|thumb|<caption>Precipitation hardening of AuCu14Pt9Ag4 at different hardening temperatures after 50% cold working</caption>]]
</figure>