Difference between revisions of "Precious Metal Powders and Preparations"

From Electrical Contacts
Jump to: navigation, search
(Conductive Paints and Adhesives)
(Conductive Paints and Adhesives)
Line 47: Line 47:
  
 
Conductive adhesives are used mostly for mechanical bonding with low thermal impact. As the adhesive components high-polymer organic substances such as epoxy resins and mixed polymers are mostly used. They are made of electrical filler materials such as flake shaped silver powders (70 – 80 wt%). Silver based conductive adhesives are available as single or two component adhesive systems. Both types are hardening without the application of pressure.
 
Conductive adhesives are used mostly for mechanical bonding with low thermal impact. As the adhesive components high-polymer organic substances such as epoxy resins and mixed polymers are mostly used. They are made of electrical filler materials such as flake shaped silver powders (70 – 80 wt%). Silver based conductive adhesives are available as single or two component adhesive systems. Both types are hardening without the application of pressure.
 +
  
  

Revision as of 09:54, 13 December 2022

Precious Metal Powders

Precious metal powders are used as raw materials for many technical products as well as for medical and decorative applications. This includes the production of silver composites for electrical contacts (Ag/Ni, Ag/metal oxides, Ag/C, Ag/W, etc.), catalysts, electrodes or dental products. Besides these, precious metal powders are used as the base material in preparations as well as conductive paints and adhesives.

Precious metal powders consist of small particles of approx. 1 – 100 µm diameter, which distinguish themselves by particle shape, particle size and particle size distribution. Depending on the manufacturing process, silver particles may be spherical, crystalline or dentritic. Smaller particle size typically leads to a larger surface area.

The measured densities of powders – both, the apparent density and the tap density – are low, compared to the wrought metals because of the gaps between the particles. They vary in a wide range between 0.5 and 6 g/cm3 depending on the morphology of the particles and their tendency to agglomeration. Precious metal powders can be compacted by pressing and sintering afterwards; a certain amount of porosity is however always retained.

Figure 1: Different shapes of silver powders a) spherical b) rounded crystal applomerates

Precious metal powders are produced by various methods, such as for example electrolysis, atomizing from the molten phase, chemical precipitation or by cementation with non-precious metals. Depending on the manufacturing process, silver powders – as the by far largest volume precious metal powder used – have different properties as shown in (Table 1 and Table Quality Criteria of Differently Manufactured Silver Powders). Atomizing from a melt results in a powder with high tap density composed of spherical particles. Using electrolytic deposition from a silver salt solution, creates randomly shaped dentritic to crystalline particle structures. Chemical processes can result in rather fine particles with a large specific surface area. Figure 1 shows typical SEM photographs of atomized silver powder in spherical shapes (a) and a cementation powder composed of rounded crystal agglomerates (b).


Table 1: Different Types of Silver Powders

Powder type

GE

GN1

ES

V

Manufacturing Process

chemical

chemical

electrolytic

atomized

Particle shape

agglomerated

agglomerated

dentritic

spherical

Avg. particle diameter

(median) [µm]

10 - 15

20 - 40

-

32 - 60

Medium particle size

(FSS - Fisher Sub Sieve Size) [µm]

-

-

4.0 - 6.0

-

Tap density

(DIN/ISO 3953) [g/cm3]

0.7 - 1.1

2.0 - 2.5

2.0 - 3.0

4.0 - 6.7

Specific surface area

(B.E.T.) [m2/g]

0.5 - 0.9

-

-

-

Precious Metal Preparations

Figure 2: Solar cell with print pattern of ARGONOR N920

While in the past mostly glass ware and ceramics (table china) were coated for decorative purposes with gold or platinum, precious metals have since quite a few years been applied to non-metallic substrates such as ceramics, glass or plastics to make their surfaces electrically conductive. To coat these surfaces, fine powders of the precious metal are dispersed in a carrier, containing a paint basis and organic solvents. Such preparations can be applied by screen or tampon printing, by spraying, immersion or with a paint brush.

Precious Metal Firing Preparations

The firing preparations in liquid or paste form are widely used in electrical and electronic engineering and especially in the thick-film technology (Table 2). The precious metal filler material is mostly pure silver because of its high electrical conductivity. During firing in an oxidizing atmosphere at temperatures between 400 and 850°C a well adhering and highly conductive surface layer is formed. When utilizing screen printing techniques any shapes of conductive patterns can be created (Figure 2) resulting in conductive paths with good electrical properties and high temperature stability.


Table 2: Liquid Silver Preparations for Firing Application (ARGONOR)

Preparation

Substrate

Material

Application by

Firing Temperature [°C]

Properties

Silver Content [wt%]

Argonor N92

glass, ceramics

paint brush, spray gun

530 - 650

Viscosity

500 – 1.000 mPa·s, good solderability

65

Argonor

glass,

ceramics

screen

printing

530 - 650

Viscosity

10 – 15.000 mPa·s, good solderability

65

Conductive Paints and Adhesives

Figure 3: Flexible keyboard contact pattern printed with AUROMAL 170

Conductive paints are precious metal preparations in liquid or paste form. They contain the metal filler material, fine silver particles as conductive pigments mostly in flake form, a paint compound on artificial resin basis and an organic solvent (Table 3). The solvent evaporates during drying in air or by aging at slightly elevated temperatures. This allows the silver particles to connect metallically and form conductive paths (Figure 3).

Conductive adhesives are used mostly for mechanical bonding with low thermal impact. As the adhesive components high-polymer organic substances such as epoxy resins and mixed polymers are mostly used. They are made of electrical filler materials such as flake shaped silver powders (70 – 80 wt%). Silver based conductive adhesives are available as single or two component adhesive systems. Both types are hardening without the application of pressure.






Table 3: Silver Paints, Conductive Pastes, and Conductive Adhesives
Preparation Substrate
Material
Application by Drying
[°C]
Properties Usage Amount
[g/100 cm2]
Area Resistance
[Ω/m2]
AROMAL 38 glass, plastics spraying, immersion,
paint brush
RT,
30 min
100°C
hard well conducting
Ag layer for broad applications
0.5 - 2 < 0.1
AROMAL 50 glass, wax, plastics spraying, immersion,
paint brush
10 min
RT
very flat surface,
especially for electrolytic build-up
0.5 - 2 < 0.2
AROMAL 70T plastics tampon printing 60 min
RT
hard and well conductive coating < 0.1
AROMAL 141 plastics,
paper- based plastics
screen printing 45 min
120°C
mechanically
very strong coatings
< 0.05
AROMAL 170 plastics screen printing 30 min
100°C
flexible layers,
well suited for foil materials
< 0.05
AROMAL K 5 A+B metal, glass dispenser,
screen printing
24h RT,
3h
80°C
mechanically very strong
bond connection
as alternative to soldering
< 0.1
AROMAL K 20 metal, plastics,
ceramics
dispenser,
screen printing
15 min
150°C
flexible bonds which help
decrease thermal stresses
< 0.1
DOSILAC Silver conductive paints in spray cans; can be spray painted; properties similar to those of AUROMAL 50

Conductive paints and adhesives have broad applications in electrical and electronic engineering. They are used for example for the contacting of film resistors, mounting of terminal wires, conducting electrostatic electricity or contacting components at low temperatures.

The mechanical strength of the bond connections depends mostly on the selected hardening temperature (Figure 4 ).

Figure 4: Shear force of an adhesive joint (silver adhesive AUROMAL K 20) as a function of the hardening temperature

Precious Metal Flakes

To obtain certain desired physical properties of preparations, the dispersed precious metals in flat flake-like particles (generally called "flakes") are needed. These are produced by milling fine metal powders in the presence of milling additives or agents. The properties of these metal flakes, i.e. silver flakes (ability to disperse easily, flow characteristics, electrical conductivity) are strongly dependent on the particle shape and size as well as on the type of milling agents used. (Figure 5) illustrates through SEM photos a type of rather fine silver flake (medium particle size 4 – 6 µm) (a) and another one with relatively large flat but thin flake shapes (particle size 8 – 11 µm) (b). Typical commercial silver flake types are listed with their respective properties in (Table 4). Gold and platinum can also be produced as powder flakes. However, in terms of the quantities used, they are of lesser economic importance.

Figure 5: SEM photos of silver flakes (a) fine grain (b) large flat





Table 4: Typical Commercial Silver Flake Types
Type of Flake F56 B190 ES4
Main characteristics Low tap density Very fine Pure, wide grain size distribution
Silver content [wt%] > 99.0 > 99.0 > 99.7
Med. Grain size [μm] Tap density 3 - 8 4 - 6 9 - 13
DIN/ISO 3953 [g/cm3] 0.7 - 1.1 2.1 - 2.7 2.7 - 3.6
Spec. Surface area B.E.T. [m2/g] 0.7 - 1.1 0.3 - 0.7