<xr id="tab:Overview_of_the_Most_Widely_Used_Silver_Grades"/><!--(Table 2.11 )--> shows the typically available quality grades of silver. In certain economic areas, i.e. China, there are additional grades with varying amounts of impurities available on the market. In powder form silver is used for a wide variety of silver based composite contact materials. Different manufacturing processes result in different grades of Ag powder as shown in <xr id="tab:Quality_Criteria_of_Differently_Manufactured_Silver_Powders"/><!--Table 2.12-->. additional Additional properties of silver powders and their usage are described in chapter [[ Precious Metal Powders and Preparations#Precious_Metal_Powders|Precious Metal Powders ]] und [[Precious_Metal_Powders_and_Preparations|Table Different Types of Silver Powders.]]<!--(Tab. 8.1.)--> Semi-finished silver materials can easily be warm or cold formed and can be clad to the usual base materials(<xr id="fig:Strain hardening of Ag bei cold working"/> and <xr id="fig:Softening of Ag after annealing after different degrees"/>). For attachment of silver to contact carriermaterials welding of wire or profile cut-offs and brazing are most widely applied. Besides these mechanical processes such as wire insertion (wire staking) and the riveting (staking) of solid or composite contact rivets are used in the manufacture of contact components.

currents < 2 A ''(<xr id="tab:Application Examples and Forms of Supply for Silver and Silver Alloys"/>)<!--(Table 2.16)''-->. Electroplated silver coatings are widely used to reduce the contact resistance and improve the brazing behavior of other contact materials and components.

 <figtable id="tab:Quality_Criteria_of_Differently_Manufactured_Silver_Powders"><caption>'''<!--Table 2.12: -->Quality Criteria of Differently Manufactured Silver Powders'''</caption>

Fig. 2.45: Strain hardening of Ag 99.95 <nowiki>*</nowiki> Manufactured by chemical precipitation <br /><nowiki>**</nowiki> Manufactured by cold workingelectrolytic deposition <br />[[File:Strain hardening of Ag bei cold working.jpg|right|thumb|Strain hardening <nowiki>***</nowiki> Manufactured by atomizing of Ag 99.95 bei cold working]]a melt

Fig<div class="multiple-images"> <figure id="fig:Strain hardening of Ag bei cold working">[[File:Strain hardening of Ag bei cold working. 2jpg|left|thumb|<caption>Strain hardening of Ag 99.4695 - cold working</caption>]]</figure> <figure id="fig: Softening of Ag 99.95 after annealing for 1 hr after different degrees of strain hardening">[[File:Softening of Ag after annealing after different degrees.jpg|rightleft|thumb|<caption>Softening of Ag 99.95 after annealing for 1 hr after different degrees of strain hardening</caption>]]</figure></div><div class="clear"></div>

To improve the physical and contact properties of fine silver , melt-metallurgical produced silver alloys are used ''(<xr id="tab:Physical Properties of Silver and Silver Alloys"/>)<!--(Table 2.13)''-->. By adding metal components , the mechanical properties such as hardness and tensile strength as well as typical contact properties such as erosion resistance, and resistance against material transfer in DC circuits are increased ''(<xr id="tab:Mechanical Properties of Silver and Silver Alloys"/>)<!--(Table 2.14)''-->. On the other hand however, other properties such as electrical conductivity and chemical corrosion resistance can be negatively impacted by alloying ''(Figs<xr id="fig:Influence of 1 10 atom of different alloying metals"/><!--(Fig. 2.47 )--> and <xr id="fig:Electrical resistivity p of AgCu alloys"/>)<!--(Fig. 2.48)-->. <figtable id="tab:Physical Properties of Silver and Silver Alloys"><caption>'''<!--Table 2.13:-->Physical Properties of Silver and Silver Alloys'''</caption> {| class="twocolortable" style="text-align: left; font-size: 12px"|-!Material !Silver Content<br />[wt%]!Density<br />[g/cm³]!Melting Point<br />or Range<br />[°C]!Electrical<br />Resistivity<br />[μΩ·cm]!Electrical<br />Conductivity<br />[MS/m]!Thermal<br />Conductivity<br />[W/mK]!Temp. Coefficient of<br />the Electr.Resistance<br />[10^-3/K]!Modulus of<br />Elasticity<br />[GPa]|-|Ag|99.95|10.5|961|1.67|60|419|4.1|80|-|AgNi0.15|99.85|10.5|960|1.72|58|414|4.0|82|-|AgCu3|97|10.4|900 - 938|1.92|52|385|3.2|85|-|AgCu5|95|10.4|910|1.96|51|380|3.0|85|-|AgCu10|90|10.3|870|2.0|50|335|2.8|85|-|AgCu28|72|10.0|779|2.08|48|325|2.7|92|-|Ag98CuNi<br />ARGODUR 27|98|10.4|940|1.92|52|385|3.5|85|-|AgCu24.5Ni0.5|75|10.0|805|2.20|45|330|2.7|92|-|Ag99.5NiMg<br />ARGODUR 32<br />Not heat treated|99.5|10.5|960|2.32|43|293|2.3|80|-|ARGODUR 32<br />Heat treated|99.5|10.5|960|2.32|43|293|2.1|80|}</figtable> <div class="multiple-images"> <figure id="fig:Influence of 1 10 atom of different alloying metals">[[File:Influence of 1 10 atom of different alloying metals.jpg|left|thumb|<caption>Influence of 1-10 atom% of different alloying metals on the electrical resistivity of silver</caption>]]</figure> <figure id="fig:Electrical resistivity p of AgCu alloys">[[File:Electrical resistivity p of AgCu alloys.jpg|left|thumb|<caption>Electrical resistivity p of AgCu alloys with 0-20 weight% Cu in the soft annealed and tempered stage a) Annealed and quenched b) Tempered at 280°C</caption>]]</figure></div><div class="clear"></div> <figtable id="tab:Mechanical Properties of Silver and Silver Alloys"><caption>'''<!--Table 2.14:-->Mechanical Properties of Silver and Silver Alloys'''</caption><table class="twocolortable"><tr><th><p class="s12">Material</p></th><th><p class="s12">Hardness</p><p class="s12">Condition</p></th><th><p class="s12">Tensile Strength</p><p class="s12">R<span class="s31">m </span>[MPa]</p></th><th><p class="s12">Elongation A [%] min.</p></th><th><p class="s12">Vickers Hardness</p><p class="s12">HV 10</p></th></tr><tr><td><p class="s12">Ag</p></td><td><p class="s12">R 200</p><p class="s12">R 250</p><p class="s12">R 300</p><p class="s12">R 360</p></td><td><p class="s12">200 - 250</p><p class="s12">250 - 300</p><p class="s12">300 - 360</p><p class="s12">&gt; 360</p></td><td><p class="s12">30</p><p class="s12">8</p><p class="s12">3</p><p class="s12">2</p></td><td><p class="s12">30</p><p class="s12">60</p><p class="s12">80</p><p class="s12">90</p></td></tr><tr><td><p class="s12">AgNi0.15</p><p class="s12"></p></td><td><p class="s12">R 220</p><p class="s12">R 270</p><p class="s12">R 320</p><p class="s12">R 360</p></td><td><p class="s12">220 - 270</p><p class="s12">270 - 320</p><p class="s12">320 - 360</p><p class="s12">&gt; 360</p></td><td><p class="s12">25</p><p class="s12">6</p><p class="s12">2</p><p class="s12">1</p></td><td><p class="s12">40</p><p class="s12">70</p><p class="s12">85</p><p class="s12">100</p></td></tr><tr><td><p class="s12">AgCu3</p></td><td><p class="s12">R 250</p><p class="s12">R 330</p><p class="s12">R 400</p><p class="s12">R 470</p></td><td><p class="s12">250 - 330</p><p class="s12">330 - 400</p><p class="s12">400 - 470</p><p class="s12">&gt; 470</p></td><td><p class="s12">25</p><p class="s12">4</p><p class="s12">2</p><p class="s12">1</p></td><td><p class="s12">45</p><p class="s12">90</p><p class="s12">115</p><p class="s12">120</p></td></tr><tr><td><p class="s12">AgCu5</p></td><td><p class="s12">R 270</p><p class="s12">R 350</p><p class="s12">R 460</p><p class="s12">R 550</p></td><td><p class="s12">270 - 350</p><p class="s12">350 - 460</p><p class="s12">460 - 550</p><p class="s12">&gt; 550</p></td><td><p class="s12">20</p><p class="s12">4</p><p class="s12">2</p><p class="s12">1</p></td><td><p class="s12">55</p><p class="s12">90</p><p class="s12">115</p><p class="s12">135</p></td></tr><tr><td><p class="s12">AgCu10</p></td><td><p class="s12">R 280</p><p class="s12">R 370</p><p class="s12">R 470</p><p class="s12">R 570</p></td><td><p class="s12">280 - 370</p><p class="s12">370 - 470</p><p class="s12">470 - 570</p><p class="s12">&gt; 570</p></td><td><p class="s12">15</p><p class="s12">3</p><p class="s12">2</p><p class="s12">1</p></td><td><p class="s12">60</p><p class="s12">95</p><p class="s12">130</p><p class="s12">150</p></td></tr><tr><td><p class="s12">AgCu28</p></td><td><p class="s12">R 300</p><p class="s12">R 380</p><p class="s12">R 500</p><p class="s12">R 650</p></td><td><p class="s12">300 - 380</p><p class="s12">380 - 500</p><p class="s12">500 - 650</p><p class="s12">&gt; 650</p></td><td><p class="s12">10</p><p class="s12">3</p><p class="s12">2</p><p class="s12">1</p></td><td><p class="s12">90</p><p class="s12">120</p><p class="s12">140</p><p class="s12">160</p></td></tr><tr><td><p class="s12">Ag98CuNi</p><p class="s12">ARGODUR 27</p></td><td><p class="s12">R 250</p><p class="s12">R 310</p><p class="s12">R 400</p><p class="s12">R 450</p></td><td><p class="s12">250 - 310</p><p class="s12">310 - 400</p><p class="s12">400 - 450</p><p class="s12">&gt; 450</p></td><td><p class="s12">20</p><p class="s12">5</p><p class="s12">2</p><p class="s12">1</p></td><td><p class="s12">50</p><p class="s12">85</p><p class="s12">110</p><p class="s12">120</p></td></tr><tr><td><p class="s12">AgCu24,5Ni0,5</p></td><td><p class="s12">R 300</p><p class="s12">R 600</p></td><td><p class="s12">300 - 380</p><p class="s12">&gt; 600</p></td><td><p class="s12">10</p><p class="s12">1</p></td><td><p class="s12">105</p><p class="s12">180</p></td></tr><tr><td><p class="s12">Ag99,5NiMg</p><p class="s12">ARGODUR 32</p><p class="s12">Not heat treated</p></td><td><p class="s12">R 220</p><p class="s12">R 260</p><p class="s12">R 310</p><p class="s12">R 360</p></td><td><p class="s12">220</p><p class="s12">260</p><p class="s12">310</p><p class="s12">360</p></td><td><p class="s12">25</p><p class="s12">5</p><p class="s12">2</p><p class="s12">1</p></td><td><p class="s12">40</p><p class="s12">70</p><p class="s12">85</p><p class="s12">100</p></td></tr><tr><td><p class="s12">ARGODUR 32 Heat treated</p></td><td><p class="s12">R 400</p></td><td><p class="s12">400</p></td><td><p class="s12">2</p></td><td><p class="s12">130-170</p></td></tr></table></figtable>

Fine-Grain Silver (ARGODUR-Spezial) silver is defined as a silver alloy with an addition of 0.15 wt% of Nickelnickel. Silver and nickel are not soluble in each other in solid form. In liquid silver , only a small amount of nickel is soluble as the phase diagram ''illustrates (<xr id="fig:Phase diagram of silver nickel"/><!--(Fig. 2.51)'' illustrates-->). During solidification of the melt , this nickel addition gets finely dispersed in the silver matrix and eliminates the pronounce coarse grain growth after prolonged influence of elevated temperatures ''(Figs<xr id="fig:Coarse grain micro structure of Ag"/><!--(Fig. 2.49 )--> and <xr id="fig:Fine grain microstructure of AgNiO"/><!--(Fig. 2.50)''-->). <div class="multiple-images"> <figure id="fig:Coarse grain micro structure of Ag">[[File:Coarse grain micro structure of Ag.jpg|left|thumb|<caption>Coarse grain micro structure of Ag 99.97 after 80% cold working and 1 hr annealing at 600°C</caption>]]</figure>

Fig. 2.49<figure id="fig: Coarse Fine grain micro structure microstructure of Ag 99.97 after 80% cold working and 1 hr annealing at 600°CAgNiO">[[File:Coarse Fine grain micro structure microstructure of AgAgNiO.jpg|rightleft|thumb|Coarse <caption>Fine grain micro structure microstructure of Ag 99AgNi0.97 15 after 80% cold working and 1 hr annealing at 600°C</caption>]]</figure>

Fig. 2.50<figure id="fig: Fine grain microstructure Phase diagram of AgNi0.15 after 80% cold working and 1 hr annealing at 600°Csilver nickel">[[File:Fine grain microstructure Phase diagram of AgNiOsilver nickel.jpg|rightleft|thumb|Fine grain microstructure <caption>Phase diagram of AgNi0.15 after 80% cold working and 1 hr annealing at 600°Csilver nickel</caption>]]</figure></div><div class="clear"></div>

Fine-grain Grain silver has almost the same chemical corrosion resistance as fine silver. Compared to pure silver , it exhibits a slightly increased hardness andtensile strength ''(<xr id="tab:Mechanical Properties of Silver and Silver Alloys"/><!--(Table 2.14)''-->). The electrical conductivity is just slightly decreased by this low nickel addition. Because of its significantly improved contact properties , fine grain silver has replaced pure silver in many applications.

Using copper as an alloying component increases the mechanical stability of silver significantly(<xr id="fig:Strain hardening of AgCu3 by cold working"/>, <xr id="fig:Softening of AgCu3 after annealing"/> and <xr id="fig:Strain hardening of AgCu5 by cold working"/>). The most important among the binary AgCu alloys is that of AgCu3, known in europe also under the name of known as hard-silver. This material still has a chemical corrosion resistance close to that of fine silver. In comparison to pure silver and fine-grain silver , AgCu3 exhibits increased mechanical strength as well as higher arc erosion resistance and mechanical wear resistance ''(Table 2.14)''.

Increasing the Cu content further also increases the mechanical strength of AgCu alloys and improves arc erosion resistance and resistance against material transfer while at the same time however simultaneously the tendency to oxide formation becomes detrimental. This causes - during switching under arcing conditions - an increase in contact resistance with rising numbers of operation. In special applications , where highest mechanical strength is recommended and a reduced chemical resistance can be tolerated, the eutectic AgCu alloy with 28 wt% of copper ''is used (<xr id="fig:Phase diagram of silver copper"/>)<!--(Fig. 2.52)'' is used-->. AgCu10 , also known as coin silver , has been replaced in many applications by composite silver-based materials while sterling silver (AgCu7.5) has never extended its important usage from decorative table wear and jewelry to industrial applications in electrical contacts.

Besides these binary alloys, ternary AgCuNi alloys are used in electrical contact applications. From this group , the material ARGODUR 27, an alloy of 98 wt% Ag with a 2 wt% Cu and nickel addition has found practical importance close to that of AgCu3. This material is characterized by high resistance to oxidation and low tendency to re-crystallization during exposure to high temperatures. Besides high mechanical stability this AgCuNi alloy also exhibits a strong resistance against arc erosion. Because of its high resistance against material transfer , the alloy AgCu24.5Ni0.5 has been used in the automotive industry for an extended time in the North American market. Caused by miniaturization and the related reduction in available contact forces in relays and switches , this material has been replaced widely because of its tendency to oxide formation.

Hard-silver alloys are widely used for switching applications in the information and energy technology for currents up to 10 A, in special cases also for higher current ranges ''(<xr id="tab:Application Examples and Forms of Supply for Silver and Silver Alloys"/>)<!--(Table 2.16)''-->. Dispersion hardened alloys of silver with 0.5 wt% MgO and NiO (ARGODUR 32) are produced by internal oxidation. While the melt-metallurgical alloy is easy to cold-work and form, the material becomes very hard and brittle after dispersion hardening. Compared to fine silver and hard-silver, this material has a greatly improved temperature stability and can be exposed to brazing temperatures up to 800°C without decreasing its hardness and tensile strength.Because of these mechanical properties and its high electrical conductivity ARGODUR 32 is mainly used in the form of contact springs that are exposed to high thermal and mechanical stresses in relays and contactors for aeronautic applications. <div class="multiple-images"> <figure id="fig:Phase diagram of silver copper"> [[File:Phase diagram of silver copper.jpg|left|thumb|<caption>Phase diagram of silver-copper</caption>]]</figure> <figure id="fig:Strain hardening of AgCu3 by cold working"> [[File:Strain hardening of AgCu3 by cold working.jpg|left|thumb|<caption>Strain hardening of AgCu3 by cold working</caption>]]</figure> <figure id="fig:Softening of AgCu3 after annealing"> [[File:Softening of AgCu3 after annealing.jpg|left|thumb|<caption>Softening of AgCu3 after annealing for 1 hr after 80% cold working</caption>]]</figure> <figure id="fig:Strain hardening of AgCu5 by cold working"> [[File:Strain hardening of AgCu5 by cold working.jpg|left|thumb|<caption>Strain hardening of AgCu5 by cold working</caption>]]</figure> <figure id="fig:Softening of AgCu5 after annealing"> [[File:Softening of AgCu5 after annealing.jpg|left|thumb|<caption>Softening of AgCu5 after annealing for 1 hr after 80% cold working</caption>]]</figure>  <figure id="fig:Strain hardening of AgCu 10 by cold working"> [[File:Strain hardening of AgCu 10 by cold working.jpg|left|thumb|<caption>Strain hardening of AgCu 10 by cold working</caption>]]</figure>

Dispersion hardened alloys <figure id="fig:Softening of silver with 0.5 wt% MgO and NiO (ARGODUR 32) are produced by internal oxidation. While the melt-metallurgical alloy is easy to cold-work and form the material becomes very hard and brittle AgCu10 after dispersion hardening. Compared to fine silver and hard-silver this material has a greatly improved temperature stability and can be exposed to brazing temperatures up to 800°C without decreasing its hardness and tensile strength.annealing"> Because [[File:Softening of these mechanical properties and its high electrical conductivity ??? ARGODUR 32 is mainly used in the form AgCu10 after annealing.jpg|left|thumb|<caption>Softening of contact springs that are exposed to high thermal and mechanical stresses in relays, and contactors AgCu10 after annealing for aeronautic applications.1 hr after 80% cold working</caption>]]</figure>

'''Table 2<figure id="fig:Strain hardening of AgCu28 by cold working"> [[File:Strain hardening of AgCu28 by cold working.13: Physical Properties jpg|left|thumb|<caption>Strain hardening of Silver and Silver Alloys'''AgCu28 by cold working</caption>]]</figure>

Fig. 2.51<figure id="fig: Phase diagram Softening of silver-nickelAgCu28 after annealing"> [[File:Phase diagram Softening of silver nickelAgCu28 after annealing.jpg|rightleft|thumb|Phase diagram <caption>Softening of silver nickelAgCu28 after annealing for 1 hr after 80% cold working</caption>]]</figure>

Fig. 2.52: Phase diagram of silver-copper[[File:Phase diagram of silver copper.jpg|right|thumb|Phase diagram of silver-copper]]Fig. 2.53: Phase diagram of silver-cadmium[[File:Phase diagram of silver cadmium.jpg|right|thumb|Phase diagram of silver-cadmium]]Fig. 2.54<figure id="fig: Strain hardening of AgCu3 AgNi0.15 by cold working"> [[File:Strain hardening of AgCu3 AgNiO15 by cold working.jpg|rightleft|thumb|<caption>Strain hardening of AgCu3 AgNiO15 by cold working</caption>]]</figure>

'''Table 2.14: Mechanical Properties of Silver and Silver Alloys'''<table border="1" cellspacingfigure id="0" style="border-collapsefig:collapseSoftening of AgNi0.15 after annealing"><tr><td><p class="s12">Material/</p><p class="s12">DODUCO-Designation</p></td><td><p class="s12">Hardness</p><p class="s12">Condition</p></td><td><p class="s12">Tensile Strength</p><p class="s12">R<span class="s31">m </span>[MPa]</p></td><td><p class="s12">Elongation A [%] minFile:Softening of AgNiO15 after annealing.jpg|left|thumb|</pcaption>Softening of AgNiO15 after annealing</td><td><p class="s12">Vickers Hardness</p><p class="s12">HV 10</p></td></tr><tr><td><p class="s12">Ag</p></td><td><p class="s12">R 200</p><p class="s12">R 250</p><p class="s12">R 300</p><p class="s12">R 360</p></td><td><p class="s12">200 - 250</p><p class="s12">250 - 300</p><p class="s12">300 - 360</p><p class="s12">&gt; 360</p></td><td><p class="s12">30</p><p class="s12">8</p><p class="s12">3</p><p class="s12">2</p></td><td><p class="s12">30</p><p class="s12">60</p><p class="s12">80</p><p class="s12">90</p></td></tr><tr><td><p class="s12">AgNi 0,15</p><p class="s12">ARGODUR Special</p></td><td><p class="s12">R 220</p><p class="s12">R 270</p><p class="s12">R 320</p><p class="s12">R 360</p></td><td><p class="s12">220 - 270</p><p class="s12">270 - 320</p><p class="s12">320 - 360</p><p class="s12">&gt; 360</p></td><td><p class="s12">25</p><p class="s12">6</p><p class="s12">2</p><p class="s12">1</p></td><td><p class="s12">40</p><p class="s12">70</p><p class="s12">85</p><p class="s12">100</p></td></tr><tr><td><p class="s12">AgCu3</p></td><td><p class="s12">R 250</p><p class="s12">R 330</p><p class="s12">R 400</p><p class="s12">R 470</p></td><td><p class="s12">250 - 330</p><p class="s12">330 - 400</p><p class="s12">400 - 470</p><p class="s12">&gt; 470</p></td><td><p class="s12">25</p><p class="s12">4</p><p class="s12">2</p><p class="s12">1</p></td><td><p class="s12">45</p><p class="s12">90</p><p class="s12">115</p><p class="s12">120</p></td></tr><tr><td><p class="s12">AgCu5</p></td><td><p class="s12">R 270</p><p class="s12">R 350</p><p class="s12">R 460</p><p class="s12">R 550</p></td><td><p class="s12">270 - 350</p><p class="s12">350 - 460</p><p class="s12">460 - 550</p><p class="s12">&gt; 550</p></td><td><p class="s12">20</p><p class="s12">4</p><p class="s12">2</p><p class="s12">1</p></td><td><p class="s12">55</p><p class="s12">90</p><p class="s12">115</p><p class="s12">135</p></td></tr><tr><td><p class="s12">AgCu10</p></td><td><p class="s12">R 280</p><p class="s12">R 370</p><p class="s12">R 470</p><p class="s12">R 570</p></td><td><p class="s12">280 - 370</p><p class="s12">370 - 470</p><p class="s12">470 - 570</p><p class="s12">&gt; 570</p></td><td><p class="s12">15</p><p class="s12">3</p><p class="s12">2</p><p class="s12">1</p></td><td><p class="s12">60</p><p class="s12">95</p><p class="s12">130</p><p class="s12">150</p></td></tr><tr><td><p class="s12">AgCu28</p></td><td><p class="s12">R 300</p><p class="s12">R 380</p><p class="s12">R 500</p><p class="s12">R 650</p></td><td><p class="s12">300 - 380</p><p class="s12">380 - 500</p><p class="s12">500 - 650</p><p class="s12">&gt; 650</p></td><td><p class="s12">10</p><p class="s12">3</p><p class="s12">2</p><p class="s12">1</p></td><td><p class="s12">90</p><p class="s12">120</p><p class="s12">140</p><p class="s12">160</p></td></tr><tr><td><p class="s12">Ag98CuNi</p><p class="s12">ARGODUR 27</p></td><td><p class="s12">R 250</p><p class="s12">R 310</p><p class="s12">R 400</p><p class="s12">R 450</p></td><td><p class="s12">250 - 310</p><p class="s12">310 - 400</p><p class="s12">400 - 450</p><p class="s12">&gt; 450</p></td><td><p class="s12">20</p><p class="s12">5</p><p class="s12">2</p><p class="s12">1</p></td><td><p class="s12">50</p><p class="s12">85</p><p class="s12">110</p><p class="s12">120</p></td></tr><tr><td><p class="s12">AgCu24,5Ni0,5</p></td><td><p class="s12">R 300</p><p class="s12">R 600</p></td><td><p class="s12">300 - 380</p><p class="s12">&gt; 600</p></td><td><p class="s12">10</p><p class="s12">1</p></td><td><p class="s12">105</p><p class="s12">180</p></td></tr><tr><td><p class="s12">AgCd10</p></td><td><p class="s12">R 200</p><p class="s12">R 280</p><p class="s12">R 400</p><p class="s12">R 450</p></td><td><p class="s12">200 - 280</p><p class="s12">280 - 400</p><p class="s12">400 - 450</p><p class="s12">&gt; 450</p></td><td><p class="s12">15</p><p class="s12">3</p><p class="s12">2</p><p class="s12">1</p></td><td><p class="s12">36</p><p class="s12">75</p><p class="s12">100</p><p class="s12">115</p></td></tr><tr><td><p class="s12">Ag99,5NiMg</p><p class="s12">ARGODUR 32</p><p class="s12">Not heat treated</p></td><td><p class="s12">R 220</p><p class="s12">R 260</p><p class="s12">R 310</p><p class="s12">R 360</p></td><td><p class="s12">220</p><p class="s12">260</p><p class="s12">310</p><p class="s12">360</p></td><td><p class="s12">25</p><p class="s12">5</p><p class="s12">2</p><p class="s12">1</p></td><td><p class="s12">40</p><p class="s12">70</p><p class="s12">85</p><p class="s12">100</p></td></tr><tr><td><p class="s12">ARGODUR 32 Heat treated</p></td><td><p class="s12">R 400</p></td><td><p class="s12">400</p></td><td><p class="s12">2</p></td><td><p class="s12">130-170</p></td></trcaption>]]</tablefigure>

Fig. 2.55: Softening of AgCu3 after annealing for 1 hr after 80% cold working[[File:Softening of AgCu3 after annealing.jpg|right|thumb|Softening of AgCu3 after annealing for 1 hr after 80% cold working]]Fig. 2.56: Strain hardening of AgCu5 by cold working[[File:Strain hardening of AgCu5 by cold working.jpg|right|thumb|Strain hardening of AgCu5 by cold working]]Fig. 2.57: Softening of AgCu5 after annealing for 1 hr after 80% cold working[[File:Softening of AgCu5 after annealing.jpg|right|thumb|Softening of AgCu5 after annealing for 1 hr after 80% cold working]]Fig. 2.58: Strain hardening of AgCu 10 by cold working[[File:Strain hardening of AgCu 10 by cold working.jpg|right|thumb|Strain hardening of AgCu 10 by cold working]]Fig. 2.59: Softening of AgCu10 after annealing for 1 hr after 80% cold working[[File:Softening of AgCu10 after annealing.jpg|right|thumb|Softening of AgCu10 after annealing for 1 hr after 80% cold working]]Fig. 2.60: Strain hardening of AgCu28 by cold working[[File:Strain hardening of AgCu28 by cold working.jpg|right|thumb|Strain hardening of AgCu28 by cold working]]Fig. 2.61: Softening of AgCu28 after annealing for 1 hr after 80% cold working[[File:Softening of AgCu28 after annealing.jpg|right|thumb|Softening of AgCu28 after annealing for 1 hr after 80% cold working]]Fig. 2.62: Strain hardening of AgNi0.15 by cold working[[File:Strain hardening of AgNiO15 by cold working.jpg|right|thumb|Strain hardening of AgNiO15 by cold working]]Fig. 2.63: Softening of AgNi0.15 after annealing for 1 hr after 80% cold working[[File:Softening of AgNiO15 after annealing.jpg|right|thumb|Softening of AgNiO15 after annealing]]Fig. 2.64<figure id="fig: Strain hardening of ARGODUR 27 by cold working"> [[File:Strain hardening of ARGODUR 27.jpg|rightleft|thumb|<caption>Strain hardening of AgCu1.8Ni0.2 (ARGODUR 27 ) by cold working</caption>]]Fig. 2.65: Softening of ARGODUR 27 after annealing for 1 hr after 80% cold working[[File:Softening of ARGODUR 27 after annealing.jpg|right|thumb|Softening of ARGODUR 27 after annealing for 1 hr after 80% cold working]]</figure>

<figure id="fig:Softening of ARGODUR 27 after annealing"> [[File:Softening of ARGODUR 27 after annealing.jpg|left|thumb|<caption>Softening of AgCu1.8Ni0.2 (ARGODUR 27) after annealing for 1 hr after 80% cold working</caption>]]</figure></div><div class="clear"></div>   <figtable id="tab:Contact and Switching Properties of Silver and Silver Alloys"><caption>'''<!--Table 2.15: -->Contact and Switching Properties of Silver and Silver Alloys'''</caption>

|Ag<br />AgNi0,.15<br />ARGODUR-Special

Cu content, compared to fine Ag higher arc erosion resistance and mechanical strength, lower tendency to materialtransfer

 <figtable id="tab:Application Examples and Forms of Supply for Silver and Silver Alloys"><caption>'''<!--Table 2.16: -->Application Examples and Forms of Supply for Silver and Silver Alloys'''</caption>

|Ag<br />AgNi0,.15<br />ARGODUR-Spezial<br />AgCu3<br />AgNi98NiCu2<br />ARGODUR 27<br />AgCu24,5Ni0,5|Relays,<br />Micro switches,<br />Auxiliary current switches,<br />Control circuit devices,<br />Appliance switches,<br />Wiring devices (< &le; 20A),<br />Main switches

|Ag99, .5NiOMgO<br />ARGODUR 32

The addition of 30 wt% Pd increases the mechanical properties as well as the resistance of silver against the influence of sulfur and sulfur containingcompounds significantly ''(Tables <xr id="tab:Physical Properties of Silver-Palladium Alloys"/><!--(Tab 2.17 )--> and <xr id="tab:Mechanical Properties of Silver-Palladium Alloys"/>)<!--(Tab.2.18)''-->. Alloys with 40-60 wt% Pd have an even higher resistance against silver sulfide formation. At these percentage ranges however , the catalytic properties of palladium can influence the contact resistance behavior negatively. The formability also decreases with increasing Pd contents.

AgPd alloys are hard, arc erosion resistant, and have a lower tendency towards material transfer under DC loads ''(<xr id="tab:Contact and Switching Properties of Silver-Palladium Alloys"/>)<!--(Table 2.19)''-->. On the other hand , the electrical conductivity is decreased at higher Pd contents. The ternary alloy AgPd30Cu5 has an even higher hardness , which makes it suitable for use in sliding contact systems.

AgPd alloys are mostly used in relays for the switching of medium to higher loads (>60V, >2A) as shown in <xr id="tab:Application Examples and Forms of Suppl for Silver-Palladium Alloys"/><!--(Table 2.20)-->. Because of the high palladium price , these formerly solid contacts have been widely replaced by multi-layer designs such as AgNi0.15 or AgNi10 with a thin Au surface layer. A broader field of application for AgPd alloys remains in the wear resistant sliding contact systems.

'''Table 2.18: Mechanical Properties of Silver-Palladium Alloys'''<table border="1" cellspacing="0" stylediv class="bordermultiple-collapse:collapseimages"><tr><td><p classfigure id="s12fig:Phase diagram of silver palladium">Material</p></td><td><p class="s12">Hardness</p><p class="s12">Condition</p></td><td><p class="s12">Tensile Strength</p><p class="s12">R<span class="s31">m </span>[MPa]</p></td><td><p class="s12">Elongation A</p><p class="s12">[%]minFile:Phase diagram of silver palladium.jpg|left|thumb|</pcaption>Phase diagram of silver-palladium</td><td><p class="s12">Vickers Hardness</p><p class="s12">HV</p></td></tr><tr><td><p class="s12">AgPd30</p></td><td><p class="s12">R 320</p><p class="s12">R 570</p></td><td><p class="s12">320</p><p class="s12">570</p></td><td><p class="s12">38</p><p class="s12">3</p></td><td><p class="s12">65</p><p class="s12">145</p></td></tr><tr><td><p class="s12">AgPd40</p></td><td><p class="s12">R 350</p><p class="s12">R 630</p></td><td><p class="s12">350</p><p class="s12">630</p></td><td><p class="s12">38</p><p class="s12">2</p></td><td><p class="s12">72</p><p class="s12">165</p></td></tr><tr><td><p class="s12">AgPd50</p></td><td><p class="s12">R 340</p><p class="s12">R 630</p></td><td><p class="s12">340</p><p class="s12">630</p></td><td><p class="s12">35</p><p class="s12">2</p></td><td><p class="s12">78</p><p class="s12">185</p></td></tr><tr><td><p class="s12">AgPd60</p></td><td><p class="s12">R 430</p><p class="s12">R 700</p></td><td><p class="s12">430</p><p class="s12">700</p></td><td><p class="s12">30</p><p class="s12">2</p></td><td><p class="s12">85</p><p class="s12">195</p></td></tr><tr><td><p class="s12">AgPd30Cu5</p></td><td><p class="s12">R 410</p><p class="s12">R 620</p></td><td><p class="s12">410</p><p class="s12">620</p></td><tdcaption><p class="s12">40]]</pfigure><p class="s12">2</p></td><td><p class="s12">90</p><p class="s12">190</p></td></tr></table>'''Table 2.19: Contact and Switching Properties of Silver-Palladium Alloys'''

<figure id="fig:Strain hardening of AgPd30 by cold working">[[File:Strain hardening of AgPd30 by cold working.jpg|left|thumb|<caption>Strain hardening of AgPd30 by cold working</caption>]]</figure> <figure id="fig:Strain hardening of AgPd50 by cold working">[[File:Strain hardening of AgPd50 by cold working.jpg|left|thumb|<caption>Strain hardening of AgPd50 by cold working</caption>]]</figure> <figure id="fig:Strain hardening of AgPd30Cu5 by cold working">[[File:Strain hardening of AgPd30Cu5 by cold working.jpg|left|thumb|<caption>Strain hardening of AgPd30Cu5 by cold working</caption>]]</figure> <figure id="fig:Softening of AgPd30 AgPd50 AgPd30Cu5">[[File:Softening of AgPd30 AgPd50 AgPd30Cu5.jpg|left|thumb|<caption>Softening of AgPd30, AgPd50, and AgPd30Cu5 after annealing of 1 hr after 80% cold working</caption>]]</figure></div><div class="clear"></div>  <figtable id="tab:Physical Properties of Silver-Palladium Alloys"> <caption>'''<!--Table 2.17:--> Physical Properties of Silver-Palladium Alloys'''</caption> {| class="twocolortable" style="text-align: left; font-size: 12px"|-!Material!Palladium Content<br />[wt%]!Density<br />[g/cm³]!Melting Point<br />or Range<br />[°C]!Electrical<br />Resistivity<br />[μΩ·cm]!Electrical<br />Conductivity<br />[MS/m]!Thermal<br />Conductivity<br />[W/m·K]!Temp. Coefficient of<br />the Electr. Resistance<br />[10^-3/K]|-|AgPd30|30|10.9|1155 - 1220|14.7|6.8|60|0.4|-|AgPd40|40|11.1|1225 - 1285|20.8|4.8|46|0.36|-|AgPd50|50|11.2|1290 - 1340|32.3|3.1|34|0.23|-|AgPd60|60|11.4|1330 - 1385|41.7|2.4|29|0.12|-|AgPd30Cu5|30|10.8|1120 - 1165|15.6|6.4|28|0.37|}</figtable>  <figtable id="tab: Application Examples and Forms Mechanical Properties of Silver-Palladium Alloys"><caption>'''<!--Table 2.18:-->Mechanical Properties of Suppl for Silver-Palladium Alloys'''</caption><table class="twocolortable"><tr><th><p class="s12">Material</p></th><th><p class="s12">Hardness</p><p class="s12">Condition</p></th><th><p class="s12">Tensile Strength</p><p class="s12">R<span class="s31">_m</span>[MPa]</p></th><th><p class="s12">Elongation A</p><p class="s12">[%]min.</p></th><th><p class="s12">Vickers Hardness</p><p class="s12">HV</p></th></tr><tr><td><p class="s12">AgPd30</p></td><td><p class="s12">R 320</p><p class="s12">R 570</p></td><td><p class="s12">320</p><p class="s12">570</p></td><td><p class="s12">38</p><p class="s12">3</p></td><td><p class="s12">65</p><p class="s12">145</p></td></tr><tr><td><p class="s12">AgPd40</p></td><td><p class="s12">R 350</p><p class="s12">R 630</p></td><td><p class="s12">350</p><p class="s12">630</p></td><td><p class="s12">38</p><p class="s12">2</p></td><td><p class="s12">72</p><p class="s12">165</p></td></tr><tr><td><p class="s12">AgPd50</p></td><td><p class="s12">R 340</p><p class="s12">R 630</p></td><td><p class="s12">340</p><p class="s12">630</p></td><td><p class="s12">35</p><p class="s12">2</p></td><td><p class="s12">78</p><p class="s12">185</p></td></tr><tr><td><p class="s12">AgPd60</p></td><td><p class="s12">R 430</p><p class="s12">R 700</p></td><td><p class="s12">430</p><p class="s12">700</p></td><td><p class="s12">30</p><p class="s12">2</p></td><td><p class="s12">85</p><p class="s12">195</p></td></tr><tr><td><p class="s12">AgPd30Cu5</p></td><td><p class="s12">R 410</p><p class="s12">R 620</p></td><td><p class="s12">410</p><p class="s12">620</p></td><td><p class="s12">40</p><p class="s12">2</p></td><td><p class="s12">90</p><p class="s12">190</p></td></tr></table border></figtable>  <figtable id="1tab:Contact and Switching Properties of Silver-Palladium Alloys" cellspacing><caption>'''<!--Table 2.19:-->Contact and Switching Properties of Silver-Palladium Alloys''</caption>' {| class="0twocolortable" style="bordertext-align: left; font-collapsesize:collapse12px"|-!Material !colspan="2" | Properties|-|AgPd30-60|Corrosion resistant, tendency to Brown Powder formation increases with Pd content, low tendency to material transfer in DC circuits, high ductility |Resistant against Ag₂S formation, low contact resistance, increasing hardness with higher Pd content, AgPd30 has highest arc erosion resistance, easy to weld and clad|-|AgPd30Cu5 |High mechanical wear resistance|High Hardness |}</figtable>  <figtable id="tab:Application Examples and Forms of Suppl for Silver-Palladium Alloys"><caption>'''<!--Table 2.20:-->Application Examples and Forms of Suppl for Silver-Palladium Alloys'''</caption><table class="twocolortable"><tr><tdth><p class="s12">Material</p></tdth><tdth><p class="s12">Application Examples</p></tdth><tdth><p class="s12">Form of Supply</p></tdth></tr><tr><td><p class="s12">AgPd 30-60</p></td><td><p class="s12">Switches, relays, push-buttons,</p><p class="s12">connectors, sliding contacts</p></td><td><p class="s12">'''Semi-finished Materials:'''</p><p class="s12">Wires, micro profiles (weld tapes), clad</p><p class="s12">contact strips, seam-welded strips</p><p class="s12">'''Contact Parts:'''</p><p class="s12">Solid and composite rivets, weld buttons;</p><p class="s12">clad and welded contact parts, stamped parts</p></td></tr><tr><td><p class="s12">AgPd30Cu5</p></td><td><p class="s12">Sliding contacts, slider tracks</p></td><td><p class="s12">Wire-formed parts, contact springs, solid</p><p class="s12">and clad stamped parts</p></td></tr></table></figtable>

====Silver-Nickel (SINIDUR) Materials====Since silver and nickel are not soluble in each other in solid form and also show very limited solubility in the liquid phase have only very limited solubility , silver nickel composite materials with higher Ni contents can only be produced by powder metallurgy. During extrusion of sintered Ag/Ni billets into wires, strips and rods , the Ni particles embedded in the Ag matrix are stretched and oriented in the microstructure into a pronounced fiber structure ''(Figs<xr id="fig:Micro structure of AgNi9010"/><!--(Fig. 2.75)--> and <xr id="fig:Micro structure of AgNi 8020"/>)<!--(Fig. and 2.76)''-->

The high density produced during hot extrusion , aids the arc erosion resistance of these materials ''(Tables <xr id="tab:Physical Properties of Silver-Nickel (SINIDUR) Materials"/>)<!--(Tab 2.21 and 2.22)''-->. The typical application of Ag/Ni contact materials is in devices for switching currents of up to 100A ''(<xr id="tab:Application Examples and Forms of Supply for Silver-Nickel (SINIDUR) Materials"/>)<!--(Table 2.24)''-->. In this range , they are significantly more erosion resistant than silver or silver alloys. In addition , they exhibit with nickel contents <20 wt% a low and over their operational lifetime consistent contact resistance and good arc moving properties. In DC applications Ag/Ni materials exhibit a relatively low tendency of material transfer distributed evenly over the contact surfaces ''(<xr id="tab:Contact and Switching Properties of Silver-Nickel (SINIDUR) Materials"/>)<!--(Table 2.23)''-->.

Typically Ag/Ni (SINIDUR) materials are usually produced with contents of 10-40 wt% Ni. The most widely common used materials SINIDUR Ag/Ni 10 and SINIDUR Ag/Ni 20- and also SINIDUR Ag/Ni 15, mostly used in north america-, are easily formable and applied by cladding ''(Figs<xr id="fig:Strain hardening of AgNi9010 by cold working"/>,<!--(Fig. 2.71)--> <xr id="fig:Softening of AgNi9010 after annealing"/>,<!--(Fig. 2.72)--> <xr id="fig:Strain hardening of AgNi8020"/>, <!--(Fig. 2.73)--> <xr id="fig:Softening of AgNi8020 after annealing"/>)<!--(Fig. 2.74)''-->. They can be, without any additional welding aids, economically welded and brazed to the commonly used contact carrier materials.The (SINIDUR) Ag/Ni materials with nickel contents of 30 and 40 wt% are used in switching devices , requiring a higher arc erosion resistance and where increasesin contact resistance can be compensated through higher contact forces.

The most important applications for Ag/Ni contact materials are typically in relays, wiring devices, appliance switches, thermostatic controls, auxiliaryswitches, and small contactors with nominal currents >20A ''(<xr id="tab:Application Examples and Forms of Supply for Silver-Nickel (SINIDUR) Materials"/>)<!--(Table 2.24)''-->.

<figtable id="tab:Physical Properties of Silver-Nickel (SINIDUR) Materials"><caption>'''<!--Table 2.21: -->Physical Properties of Silver-Nickel (SINIDUR) Materials'''</caption><table borderclass="1" cellspacing="0" style="border-collapse:collapsetwocolortable"><tr><td><p class="s12"th>Material/</p><p class="s11">DODUCO <span style=" color: #151616;">Designation</span></p></td><tdth><p class="s12"th>Silver Content</pth><p class="s12">[wt%]</p></td><td><p class="s12"th>Density</pth><p class="s11">[g/cm<span class="s13">3 </span><span style=" color: #151616;">]</span></p></td><td><p class="s12"th>Melting Point</pth><p class="s12">[°C]</pth></td><td><p class="s12">Electrical</p><p class="s12">Resistivity ElectricalResistivity<i>p</i></pth><p classth colspan="s11">[µ<span class="s14">S ·</span>cm]</p></td><td><p class="s122">Electrical Resistivity</p><p class="s11">(soft)</p></tdth></tr><tr><td><p class="s12">Material/</p><p class="s11">DODUCO <span style=" color: #151616;">Designation</span></p></td><td><p class="s12"th>Silver Content</pth><p class="s12"th>[wt%]</p></td><td><p class="s12"th>Density</p><p class="s11"th>[g/cm<span class="s13"sup>3 </span><span style=" color: #151616;"sup>]</span></pth></td><td><p class="s12">Melting Point</p><p class="s12"th>[°C]</p></td><tdth><p class="s12">Electrical</p><p class="s12">Resistivity <i>p</i></p><p class="s11"th>[µ<span class="s14">S ·</span>cmµΩ·cm]</pth></td><td><p class="s11"th>[% IACS]</p></td><tdth><p class="s11"th>[MS/m]</p></tdth></tr><tr><td><p class="s11">Ag/Ni 90/10</p><p class="s11">SINIDUR 10</p></td><td><p class="s11">89 - 91</p></td><td><p class="s11">10.2 - 10.3</p></td><td><p class="s11">960</p></td><td><p class="s11">1.82 - 1.92</p></td><td><p class="s12">90 - 95</p></td><td><p class="s12">52 - 55</p></td></tr><tr><td><p class="s11">Ag/Ni 85/15</p><p class="s11">SINIDUR 15</p></td><td><p class="s11">84 - 86</p></td><td><p class="s11">10.1 - 10.2</p></td><td><p class="s11">960</p></td><td><p class="s11">1.89 - 2.0</p></td><td><p class="s12">86 - 91</p></td><td><p class="s12">50 - 53</p></td></tr><tr><td><p class="s11">Ag/Ni 80/20</p><p class="s11">SINIDUR 20</p></td><td><p class="s11">79 - 81</p></td><td><p class="s11">10.0 - 10.1</p></td><td><p class="s11">960</p></td><td><p class="s11">1.92 - 2.08</p></td><td><p class="s12">83 - 90</p></td><td><p class="s12">48 - 52</p></td></tr><tr><td><p class="s11">Ag/Ni 70/30</p><p class="s11">SINIDUR 30</p></td><td><p class="s11">69 - 71</p></td><td><p class="s11">9.8</p></td><td><p class="s11">960</p></td><td><p class="s11">2.44</p></td><td><p class="s12">71</p></td><td><p class="s12">41</p></td></tr><tr><td><p class="s11">Ag/Ni 60/40</p><p class="s11">SINIDUR 40</p></td><td><p class="s11">59 - 61</p></td><td><p class="s11">9.7</p></td><td><p class="s11">960</p></td><td><p class="s11">2.70</p></td><td><p class="s12">64</p></td><td><p class="s12">37</p></td></tr></table></figtable>

Fig. 2.71<figtable id="tab: Strain hardening of Ag/Ni 90/10 by cold working[[File:Strain hardening of AgNi9010 by cold workingtab2.jpg|right|thumb|Strain hardening of Ag/Ni 90/10 by cold working]]22">Fig. <caption>'''<!-- Table 2.72: Softening of Ag/Ni 90/10 after annealing for 1 hr after 80% cold working[[File22:Softening -->Mechanical Properties of AgNi9010 after annealing.jpg|right|thumb|Softening of Ag/Ni 90/10 after annealing for 1 hr after 80% cold working]]Fig. 2.73: Strain hardening of Ag/Ni 80/20 by cold working[[File:Strain hardening of AgNi8020.jpg|right|thumb|Strain hardening of Ag/Ni 80/20 by cold working]]Fig. 2.74: Softening of Ag/Ni 80/20 after annealing for 1 hr after 80% cold working[[File:Softening of AgNi8020 after annealing.jpg|right|thumb|Softening of Ag/Ni 80/20 after annealing for 1 hr after 80% cold working]]Fig. 2.75: Micro structure of Ag/Ni 90/10 a) perpendicular to the extrusion direction b) parallel to the extrusion direction[[File:Micro structure of AgNi9010.jpg|right|thumb|Micro structure of Ag/Ni 90/10 a) perpendicular to the extrusion direction b) parallel to the extrusion direction]]Fig. 2.76: Micro structure of Ag/Ni 80/20 a) perpendicular to the extrusion direction b) parallel t o the extrusion direction[[File:Micro structure of AgNi 8020.jpg|right|thumb|Micro structure of Ag/Ni 80Silver-Nickel Materials'''</20 a) perpendicular to the extrusion direction b) parallel to the extrusion direction]]caption>

'''Table {| class="twocolortable" style="text-align: left; font-size: 12px"|-!Material !Hardness Condition!Tensile Strength R_m [Mpa]!Elongation A (soft annealed) [%] min.!Vickers Hardness HV 10|-|Ag/Ni 90/10<br />|soft<br />R 220<br />R 280<br />R 340<br />R 400|< 250<br />220 - 280<br />280 - 340<br />340 - 400<br />> 400|25<br />20<br />3<br />2<br />1|< 50<br />50 - 70<br />65 - 90<br />85 - 105<br />> 100|-|Ag/Ni 85/15<br />|soft<br />R 300<br />R 350<br />R 380<br />R 400|< 275<br />250 - 300<br />300 - 350<br />350 - 400<br />> 400|20<br />4<br />2<br />2<br />1|< 70<br />70 - 90<br />85 - 105<br />100 - 120<br />> 115|-|Ag/Ni 80/20<br />|soft<br />R 300<br />R 350<br />R 400<br />R 450|< 300<br />300 - 350<br />350 - 400<br />400 - 450<br />> 450|20<br />4<br />2<br />2<br />1|< 80<br />80 - 95<br />90 - 110<br />100 - 125<br />> 120|-|Ag/Ni 70/30<br />|R 330<br />R 420<br />R 470<br />R 530|330 - 420<br />420 - 470<br />470 - 530<br />> 530|8<br />2<br />1<br />1|80<br />100<br />115<br />135|-|Ag/Ni 60/40<br />|R 370<br />R 440<br />R 500<br />R 580|370 - 440<br />440 - 500<br />500 - 580<br />> 580|6<br />2<br />1<br />1|90<br />110<br />130<br />150|}</figtable>  <div class="multiple-images"><figure id="fig:Strain hardening of AgNi9010 by cold working">[[File:Strain hardening of AgNi9010 by cold working.23jpg|right|thumb|<caption>Strain hardening of Ag/Ni 90/10 by cold working</caption>]]</figure> <figure id="fig: Contact and Switching Properties Softening of Silver-Nickel (SINIDURAgNi9010 after annealing">[[File:Softening of AgNi9010 after annealing.jpg|right|thumb|<caption>Softening of Ag/Ni 90/10 after annealing for 1 hr after 80% cold working</caption>]]</figure> <figure id="fig:Strain hardening of AgNi8020">[[File:Strain hardening of AgNi8020.jpg|right|thumb|<caption>Strain hardening of Ag/Ni 80/20 by cold working</caption>]]</figure> <figure id="fig:Softening of AgNi8020 after annealing">[[File:Softening of AgNi8020 after annealing.jpg|right|thumb|<caption>Softening of Ag/Ni 80/20 after annealing for 1 hr after 80% cold working</caption>]]</figure> <figure id="fig:Micro structure of AgNi9010">[[File:Micro structure of AgNi9010.jpg|right|thumb|<caption>Micro structure of Ag/Ni 90/10 a) perpendicular to the extrusion direction b) Materials'''parallel to the extrusion direction</caption>]]</figure>

<figure id="fig:Micro structure of AgNi 8020">[[File:Micro structure of AgNi 8020.jpg|right|thumb|<caption>Micro structure of Ag/Ni 80/20 a) perpendicular to the extrusion direction b) parallel to the extrusion direction</caption>]]</figure></div><div class="clear"></div>  <figtable id="tab:Contact and Switching Properties of Silver-Nickel (SINIDUR) Materials"><caption>'''<!-- Table 2.2423:-->Contact and Switching Properties of Silver-Nickel Materials'''</caption> {| class="twocolortable" style="text-align: left; font-size: 12px"|-!Material !Properties|-|Ag/Ni <br />|High arc erosion resistance at switching currents up to 100A,<br />Resistance against welding for starting current up to 100A,<br />low and over the electrical contact life nearly constant contact resistance for Ag/Ni 90/10 and Ag/Ni 80/20,<br />ow and spread-out material transfer under DC load,<br />non-conductive erosion residue on isolating components resulting in only minor change of the dielectric strength of switching devices,<br />good arc moving properties,<br />good arc extinguishing properties,<br />good or sufficient ductility depending on the Ni content,<br />easy to weld and braze|}</figtable>  <figtable id="tab: Application Examples and Forms of Supply for Silver-Nickel (SINIDUR) Materials"><caption>'''<!--Table 2.24:-->Application Examples and Forms of Supply for Silver-Nickel Materials'''</caption> {| class="twocolortable" style="text-align: left; font-size: 12px"|-!Material!Application Examples!Switching or Nominal Current!Form of Supply|-|Ag/Ni 90/10-80/20|Relays<br /> Automotive Relays - Resistive load - Motor load|> 10A<br />> 10A|rowspan="9" | '''Semi-finisched Materials:'''<br />Wires, profiles,<br />clad strips,<br />Seam-welded strips,<br />Toplay strips <br />'''Contact Parts:'''<br />Contact tips, solid<br />and composite<br />rivets, Weld buttons,<br />clad, welded,<br />brazed, and riveted<br />contact parts|-|Ag/Ni 90/10, Ag/Ni 85/15-80/20|Auxiliary current switches|&le; 100A|-|Ag/Ni 90/10-80/20|Appliance switches|&le; 50A|-|Ag/Ni 90/10|Wiring devices|&le; 20A|-|Ag/Ni 90/10|Main switches, Automatic staircase illumination switches|&le; 100A|-|Ag/Ni 90/10-80/20|Control<br />Thermostats|> 10A<br />&le; 50A|-|Ag/Ni 90/10-80/20|Load switches|&le; 20A|-|Ag/Ni 90/10-80/20|Contactors circuit breakers|&le; 100A|-|Ag/Ni 90/10-80/20<br />paired with Ag/C 97/3-96/4|Motor protective circuit breakers|&le; 40A|-|Ag/Ni 80/20-60/40<br />paired with Ag/C 96/4-95/5|Fault current circuit breakers|&le; 100A|rowspan="2" | Rods, Profiles,<br />Contact tips, Formed parts,<br />brazed and welded<br />contact parts|-|Ag/Ni 80/20-60/40<br />paired with Ag/C 96/4-95/5|Power switches|> 100A|}</figtable>

The family of silver-metal oxide contact materials includes the material groups: silver-cadmium oxide (DODURIT CdO), silver-tin oxide (SISTADOX), and silverzinc oxide (DODURIT ZnO). Because of their very good contact and switching properties like high resistance against welding, low contact resistance, and high arc erosion resistance, silver-metal oxides have gained an outstanding position in a broad field of applications. They are mainly are used in low voltage electrical switching devices like relays, installation and distribution switches, appliances, industrial controls, motor controls, and protective devices (<xr id="tab:Application Examples of Silver–Metal Oxide Materials"/>)<!--(Table 2.31)-->. *'''Silver-cadmium oxide materials''' Silver-cadmium oxide materials with 10-15 wt% are produced by both, internal oxidation and powder metallurgical methods. The manufacturing of strips and wires by internal oxidation starts with a molten alloy of silver and cadmium. During a heat treatment below it's melting point in an oxygen rich atmosphere of such a homogeneous alloy, the oxygen diffuses from the surface into the bulk of the material and oxidizes the Cd to CdO in a more or less fine particle precipitation inside the Ag matrix. The CdO particles are rather fine in the surface area and getting larger towards the center of the material (Table <xr id="fig:Micro structure of AgCdO9010"/>)<!--(Fig. 2.83)-->. During the manufacturing of Ag/CdO contact material by internal oxidation, the processes vary depending on the type of semi-finished material. For Ag/CdO wires, a complete oxidation of the AgCd wire is performed, followed by wire-drawing to the required diameter (<xr id="fig:Strain hardening of internally oxidized AgCdO9010"/><!--(Figs. 2.77)--> and <xr id="fig:Softening of internally oxidized AgCdO9010"/>)<!--(Fig. 2.1378)-->. The resulting material is used for example, in the production of contact rivets. For Ag/CdO strip materials two processes are commonly used: Cladding of an AgCd alloy strip with fine silver, followed by complete oxidation, results in a strip material with a small depletion area in the center of it''s thickness and an Ag backing suitable for easy attachment by brazing (sometimes called "Conventional Ag/CdO"). Using a technology that allows the partial oxidation of a dual-strip AgCd alloy material in a higher pressure pure oxygen atmosphere, yields a composite Ag/CdO strip material that has - besides a relatively fine CdO precipitation - also an easily brazable AgCd alloy backing. These materials are mainly used as the basis for contact profiles and contact tips. During powder metallurgical production, the powder mixed made by different processes are typically converted by pressing, sintering and extrusion to wires and strips. The high degree of deformation during hot extrusion, produces a uniform and fine dispersion of CdO particles in the Ag matrix while at the same time achieving a high density which is advantageous for good contact properties (<xr id="fig:Micro structure of AgCdO9010P"/>)<!--(Fig. 2.84)-->. To obtain a backing suitable for brazing, a fine silver layer is applied by either com-pound extrusion or hot cladding prior to or right after the extrusion. For larger contact tips, and especially those with a rounded shape, the single tip Press-Sinter-Repress process (PSR) offers economical advantages. The powder mix is pressed into a die close to the final desired shape, the "green" tips are sintered, and in most cases, the repress process forms the exact final shape while at the same time, increasing the contact density and hardness. Using different silver powders and minor additives for the basic Ag and CdO, starting materials can help influence certain contact properties for specialized applications. <div class="multiple-images"><figure id="fig:Strain hardening of internally oxidized AgCdO9010">[[File:Strain hardening of internally oxidized AgCdO9010.jpg|left|thumb|<caption>Strain hardening of internally oxidized Ag/CdO 90/10 by cold working</caption>]]</figure> <figure id="fig:Softening of internally oxidized AgCdO9010">[[File:Softening of internally oxidized AgCdO9010.jpg|left|thumb|<caption>Softening of internally oxidized (i.o.) Ag/CdO 90/10 after annealing for 1 hr after 40% cold working</caption>]]</figure>

*Silver-cadmium oxide <figure id="fig:Strain hardening of AgCdO9010P">[[File:Strain hardening of AgCdO9010P.jpg|left|thumb|<caption>Strain hardening of powder metallurgical (DODURIT p.m.) Ag/CdO) materials90/10 by cold working</caption>]]</figure>

Silver-cadmium oxide (DODURIT <figure id="fig:Softening of AgCdO9010P after annealing">[[File:Softening of AgCdO9010P after annealing.jpg|left|thumb|<caption>Softening of powder metallurgical Ag/CdO) materials with 90/10-15 wtafter annealing for 1 hr after 40% are produced by both, internal oxidation and powder metallurgical methods ''(Table 2.25)''.cold working</caption>]]</figure>

The manufacturing <figure id="fig:Strain hardening of strips and wires by internal oxidation starts with a molten alloy AgCdO8812">[[File:Strain hardening of silver and cadmiumAgCdO8812. During a heat treatment below it's melting point in a oxygen rich atmosphere in such a homogeneous alloy the oxygen diffuses from the surface into the bulk jpg|left|thumb|<caption>Strain hardening of the material and oxidizes the Cd to CdO in a more or less fine particle precipitation inside the powder metallurgical Ag matrix. The /CdO particles are rather fine in the surface area and are becoming larger further away towards the center of the material ''(Fig. 2.83)''.88/12</caption>]]</figure>

During the manufacturing <figure id="fig:Softening of Ag/CdO contact material by internal oxidation the processes vary depending on the type AgCdO8812WP after annealing">[[File:Softening of semi-finished materialAgCdO8812WP after annealing. For jpg|left|thumb|<caption>Softening of powder metallurgical Ag/CdO wires a complete oxidation of the AgCd wire is performed, followed by wire-drawing to the required diameter ''(Figs. 2.77 and 2.78)''. The resulting material is used 88/12 after annealing for example in the production 1 hr after different degrees of contact rivets. For Agcold working</CdO strip materials two processes are commonly used: Cladding of an AgCd alloy strip with fine silver followed by complete oxidation results in a strip material with a small depletion area in the center of it's thickness and a Ag backing suitable for easy attachment by brazing (sometimes called “Conventional Ag/CdO”). Using a technology that allows the partial oxidation of a dual-strip AgCd alloy material in a higher pressure pure oxygen atmosphere yields a composite Agcaption>]]</CdO strip material that has besides a relatively fine CdO precipitation also a easily brazable AgCd alloy backing ''(Fig. 2.85)''. These materials (DODURIT CdO ZH) are mainly used as the basis for contact profiles and contact tips.figure>

During powder metallurgical production the powder mixed made by different processes are typically converted by pressing, sintering and extrusion to wires<figure id="fig:Micro structure of AgCdO9010">and strips[[File:Micro structure of AgCdO9010. The high degree of deformation during hot extrusion produces a uniform and fine dispersion jpg|left|thumb|<caption>Micro structure of Ag/CdO particles in the Ag matrix while at the same time achieving a high density which is advantageous for good contact properties ''(Fig90/10 i. 2o.84a)''. To obtain a backing suitable for brazing, a fine silver layer is applied by either com-pound extrusion or hot cladding prior close to or right after the extrusion ''(Fig. 2.86surface b)''.in center area</caption>]]</figure>

For larger contact tips, and especially those with <figure id="fig:Micro structure of AgCdO9010P">[[File:Micro structure of AgCdO9010P.jpg|left|thumb|<caption>Micro structure of Ag/CdO 90/10 p.m.: a rounded shape, the single tip Press-Sinter-Repress process (PSR) offers economical advantages. Theperpendicular to extrusion direction b) parallel to extrusion direction</caption>]]powder mix is pressed in a die close to the final desired shape, the “green” tips are sintered, and in most cases the repress process forms the final exact shape while at the same time increasing the contact density and hardness.</figure>

Fig. 2.79: Strain hardening of Ag/CdO 90/10 P by cold working[[File:Strain hardening of AgCdO9010P.jpg|right|thumb|Strain hardening of Ag/CdO 90/10 P by cold working]]Fig. 2.80: Softening of Ag/CdO 90/10 P after annealing for 1 hr after 40% cold working[[File:Softening of AgCdO9010P after annealing.jpg|right|thumb|Softening of Ag/CdO 90/10 P after annealing for 1 hr after 40% cold working]]Fig. 2.81: Strain hardening of Ag/CdO 88/12 WP[[File:Strain hardening of AgCdO8812.jpg|right|thumb|Strain hardening of Ag/CdO 88/12 WP]]Fig. 2.82: Softening of Ag/CdO 88/12WP after annealing for 1 hr after different degrees of cold working[[File:Softening of AgCdO8812WP after annealing.jpg|right|thumb|Softening of Ag/CdO 88/12WP after annealing for 1 hr after different degrees of cold working]]Fig. 2.83: Micro structure of Ag/CdO 90/10 i.o. a) close to surface b) in center area[[File:Micro structure of AgCdO9010.jpg|right|thumb|Micro structure of Ag/CdO 90/10 i.o. a) close to surface b) in center area]]Fig. 2.84: Micro structure of Ag/CdO 90/10 P: a) perpendicular to extrusion direction b) parallel to extrusion direction[[File:Micro structure of AgCdO9010P.jpg|right|thumb|Micro structure of Ag/CdO 90/10 P: a) perpendicular to extrusion direction b) parallel to extrusion direction]]Fig. 2.85: Micro structure of Ag/CdO 90/10 ZH: 1) Ag/CdO layer 2) AgCd backing layer[[File:Micro structure of AgCdO9010ZH.jpg|right|thumb|Micro structure of Ag/CdO 90/10 ZH: 1) Ag/CdO layer 2) AgCd backing layer]]Fig. 2.86: Micro structure of AgCdO 88/12 WP: a) perpendicular to extrusion direction b) parallel to extrusion direction[[File:Micro structure of AgCdO8812WP.jpg|right|thumb|Micro structure of AgCdO 88/12 WP: a) perpendicular to extrusion direction b) parallel to extrusion direction]]*'''Silver–tin oxide(SISTADOX)materials'''Over the past years, many Ag/CdO contact materials have been replaced by Ag/SnO₂ based materials with 2-14 wt% SnO₂ because of the toxicity of Cadmium. This changeover was further favored by the fact that Ag/SnO₂ contacts quite often show improved contact and switching properties such as lower arc erosion, higher weld resistance, and a significant lower tendency towards material transfer in DC switching circuits ''(<xr id="tab:Contact and Switching Properties of Silver–Metal Oxide Materials"/>)<!--(Table 2.30)''-->. Ag/SnO₂ materials have been optimized for a broad range of applications by other metal oxide additives and modification in the manufacturing processes that result in different metallurgical, physical and electrical properties ''(<xr id="tab:tab2.28"/><!--(Tab. 2.28)--> and <xr id="tab:tab2.29"/>)<!--(Table 2.29)''-->.

Manufacturing of Ag/SnO₂ by ''internal oxidation'' is possible in principle, but during heat treatment of alloys containing > 5 wt% of tin in oxygen, dense oxide layers formed on the surface of the material prohibit the further diffusion of oxygen into the bulk of the material. By adding Indium or Bismuth to the alloy , the internal oxidation is possible and results in materials that typically are rather hard and brittle and may show somewhat elevated contact resistance and is limited to applications in relays. To make a ductile material with fine oxide dispersion (SISTADOX TOS F) ''(Fig. 2.114)'' it is necessary to use special process variations in oxidation and extrusion which lead to materials with improved properties in relays. Adding a brazable fine silver layer to such materials results in a semifinished material , suitable for the manufacture as smaller weld profiles(SISTADOX <xr id="fig:Micro structure of Ag SnO2 92 8 WTOS F"/>) ''<!--(Fig. 2.116)''-->. Because of their resistance to material transfer and low arc erosion , these materials find for example a broaderapplication in automotive relays ''(<xr id="tab:Application Examples of Silver–Metal Oxide Materials"/>)<!--(Table 2.31)''-->.

additives improve the wettability of the oxide particles and increase the viscosity of the Ag melt. They also provide additional benefits to the mechanical and arcing contact properties of materials in this group (<xr id="tab:tab2.26"/>)<!--(Table 2.26)-->. <figtable id="tab:tab2.26"><caption>''('<!--Table 2.26):--> Physical and Mechanical Properties as well as Manufacturing Processes and Forms of Supply of Extruded Silver-Tin Oxide Contact Materials'''</caption> {| class="twocolortable" style="text-align: left; font-size: 12px"|-!Material !Silver Content<br />[wt%]!Additives!Theoretical<br />Density<br />[g/cm³]!Electrical<br />Conductivity<br />[MS/m]!Vickers<br />Hardness<br />[HV0,1]!Tensile<br />Strength<br />[MPa]!Elongation (soft annealed)<br />A[%]min.!Manufacturing<br />Process!Form of Supply|-|Ag/SnO₂ 98/2 SPW|97 - 99|WO₃|10,4|59 ± 2|57 ± 15|215|35|Powder Metallurgy|1|-|Ag/SnO₂ 92/8 SPW|91 - 93|WO₃|10,1|51 ± 2|62 ± 15|255|25|Powder Metallurgy|1|-|Ag/SnO₂ 90/10 SPW|89 - 91|WO₃|10|47 ± 5||250|25|Powder Metallurgy|1|-|Ag/SnO₂ 88/12 SPW|87 - 89|WO₃|9.9|46 ± 5|67 ± 15|270|20|Powder Metallurgy|1|-|Ag/SnO₂ 92/8 SPW4|91 - 93|WO₃|10,1|51 ± 2|62 ± 15|255|25|Powder Metallurgy|1,2|-|Ag/SnO₂ 90/10 SPW4|89 - 91|WO₃|10|||||Powder Metallurgy|1,2|-|Ag/SnO₂ 88/12 SPW4<br />|87 - 89|WO₃|9,8|46 ± 5|80 ± 10|||Powder Metallurgy|1,2|-|Ag/SnO₂ 88/12 SPW6|87 - 89|MoO₃|9.8|42 ± 5|70 ± 10|||Powder Metallurgy|2|-|Ag/SnO₂ 97/3 SPW7|96 - 98|Bi₂O₃ and WO₃||||||Powder Metallurgy|2|-|Ag/SnO₂ 90/10 SPW7|89 - 91|Bi₂O₃ and WO₃|9,9|||||Powder Metallurgy|2|-|Ag/SnO₂ 88/12 SPW7|87 - 89|Bi₂O₃ and WO₃|9.8|42 ± 5|70 ± 10|||Powder Metallurgy|2|-|Ag/SnO₂ 98/2 PMT1|97 - 99|Bi₂O₃ and CuO|10,4|57 ± 2||215|35|Powder Metallurgy|1,2|-|Ag/SnO₂ 96/4 PMT1|95 - 97|Bi₂O₃ and CuO||||||Powder Metallurgy|1,2|-|Ag/SnO₂ 94/6 PMT1|93 - 95|Bi₂O₃ and CuO||||||Powder Metallurgy|1,2|-|Ag/SnO₂ 92/8 PMT1|91 - 93|Bi₂O₃ and CuO|10|50 ± 2|62 ± 15|240|25|Powder Metallurgy|1,2|-|Ag/SnO₂ 90/10 PMT1|89 - 91|Bi₂O₃ and CuO|10|48 ± 2|65 ± 15|240|25|Powder Metallurgy|1,2|-|Ag/SnO₂ 88/12 PMT1|87 - 89|Bi₂O₃ and CuO|9,9|46 ± 5||260|20|Powder Metallurgy|1,2|-|Ag/SnO₂ 90/10 PE|89 - 91|Bi₂O₃ and CuO|9,8|48 ± 2|55 - 100|230 - 330|28|Powder Metallurgy|1|-|Ag/SnO₂ 88/12 PE|87 - 89|Bi₂O₃ and CuO|9,7|46 ± 5|60 - 106|235 - 330|25|Powder Metallurgy|1|-|Ag/SnO₂ 88/12 PMT2|87 - 89|CuO|9,9||90 ± 10|||Powder Metallurgy|1,2|-|Ag/SnO₂ 86/14 PMT3|85 - 87|Bi₂O₃ and CuO|9,8||95 ± 10|||Powder Metallurgy|2|-|Ag/SnO₂ 94/6 LC1|93 - 95|Bi₂O₃ and In₂O₃|9,8|45 ± 5|55 ± 10|||Powder Metallurgy|2|-|Ag/SnO₂ 90/10 POX1|89 - 91|In₂O₃|9,9|50 ± 5|85 ± 15|310|25|Internal Oxidation|1,2|-|Ag/SnO₂ 90/10 POX1|87 - 89|In₂O₃|9,8|48 ± 5|90 ± 15|325|25|Internal Oxidation|1,2|-|Ag/SnO₂ 90/10 POX1|85 - 87 |In₂O₃|9,6|45 ± 5|95 ± 15|330|20|Internal Oxidation|1,2|-|}</figtable> 1 = Wires, Rods, Contact rivets, 2 = Strips, Profiles, Contact tips 

In the manufacture for the initial powder mixes , different processes are applied which provide specific advantages of the resulting materials in respect to their contact properties ''<!--[[#figures|(Figs. 2.87 43 – 2.11975)'']]-->. Some of them are described here as follows::'''a) Powder blending from single component powders''' <br> In this common process all components , including additives that are part of the powder mix , are blended as single powders. The blending is usually performed in the dry stage in blenders of different design.

:'''b) Powder blending on the basis of doped powders''' <br> For incorporation of additive oxides in the SnO₂ powder , the reactive spray process (RSV) has shown advantages. This process starts with a waterbased solution of the tin and other metal compounds. This solution is nebulized under high pressure and temperature in a reactor chamber. Through the rapid evaporation of the water , each small droplet is converted into a salt crystal and from there gets transformed by oxidation into a tin oxide particle in which the additive metals are distributed evenly as oxides. The so created doped AgSnO2 AgSnO₂ powder is then mechanically mixed with silver powder.

:'''c) Powder blending based on coated oxide powders''' <br> In this process , tin oxide powder is blended with lower meting melting additive oxides such as for example Ag₂ MoO₄ and then heat treated. The SnO₂ particles are coated in this step with a thin layer of the additive oxide.

:'''e) Powder blending based on chemically precipitated compound powders''' <br> A silver salt solution is added to a suspension of for example SnO₂ together with a precipitation agent. In a chemical reaction , silver and silver oxide respectively are precipitated around the additive metal oxide particles , who act as crystallization sites. Further chemical treatment then reduces the silver oxide with the resulting precipitated powder , being a mix of Ag and SnO₂. Further processing of these differently produced powders follows the conventional processes of pressing, sintering and hot extrusion to wires and strips. From these contact parts, contact rivets and tips are manufactured. To obtain a brazable backing, the same processes as used for Ag/CdO are applied. As for Ag/CdO, larger contact tips can also be manufactured using the press-sinter-repress (PSR) process (<xr id="tab:Physical Properties of Powder Metallurgical Silver-Metal Oxide Materials with Fine Silver Backing Produced by the Press-Sinter-Repress Process"/>)<!--(Table 2.27)-->.<div id="figures"> <div class="multiple-images"><figure id="fig:Strain hardening of AgSNO2 92 8 PE">[[File:Strain hardening of AgSNO2 92 8 PE.jpg|left|thumb|<caption>Strain hardening of Ag/SnO₂ 92/8 PE by cold working</caption>]]</figure> <figure id="fig:Softening of AgSnO2 92 8 PE"> [[File:Softening of AgSnO2 92 8 PE.jpg|left|thumb|<caption>Softening of Ag/SnO₂ 92/8 PE after annealing for 1 hr after 40% cold working</caption>]]</figure>

Further processing <figure id="fig:Strain hardening of these differently produced powders follows the conventional processes Ag SnO2 88 12 PE"> [[File:Strain hardening of pressing, sintering and hot extrusion to wires and strips. From these contact parts such as contact rivets and tips are manufactured. To obtain a brazable backing the same processes as used for Ag/CdO are appliedSnO2 88 12 PE. As for jpg|left|thumb|<caption>Strain hardening of Ag/CdO, larger contact tips can also be manufactured more economically using the press-sinter-repress (PSR) process ''(Table SnO_2.27).'' 88/12 PE by cold working</caption>]]</figure>

Fig. 2.87<figure id="fig: Strain hardening Softening of Ag/SnO<sub>2</subSnO2 88 12 PE after annealing"> 92/8 PE by cold working[[File:Strain hardening Softening of AgSNO2 92 8 Ag SnO2 88 12 PEafter annealing.jpg|rightleft|thumb|Strain hardening of Ag/SnO<sub>2</subcaption> 92/8 PE by cold working]]Fig. 2.88: Softening of Ag/SnO₂ 9288/8 12 PE after annealing for 1 hr after 40% cold working[[File:Softening of AgSnO2 92 8 PE.jpg|right|thumb|Softening of Ag</SnO<subcaption>2]]</subfigure> 92/8 PE after annealing for 1 hr after 40% cold working]]

'''Table 2.26<figure id="fig:Strain hardening of oxidized AgSnO2 88 12 PW4"> [[File: Physical and Mechanical Properties as well as Manufacturing Processes and Forms Strain hardening of Supply oxidized AgSnO2 88 12 PW4.jpg|left|thumb|<caption>Strain hardening of Extruded Silver-Tin Oxide (SISTADOX) Contact Materials'''oxidized Ag/SnO₂ 88/12 PW4 by cold working</caption>]]</figure>

Fig. 2.89: Strain hardening of Ag/SnO₂ 88/12 PE by cold working[[File:Strain hardening of Ag SnO2 88 12 PE.jpg|right|thumb|Strain hardening of Ag/SnO₂ 88/12 PE by cold working]]Fig. 2.90: Softening of Ag/SnO₂ 88/12 PE after annealing for 1 hr after 40% cold working[[Filefigure id="fig:Softening of Ag SnO2 88 12 PE PW4 after annealing.jpg|right|thumb|Softening of Ag/SnO₂ 88/12 PE after annealing for 1 hr after 40% cold working]]Fig. 2.91: Strain hardening of oxidized Ag/SnO₂ 88/12 PW4 by cold working[[File:Strain hardening of oxidized AgSnO2 88 12 PW4.jpg|right|thumb|Strain hardening of oxidized Ag/SnO₂ 88/12 PW4 by cold working]]Fig. 2.92: Softening of Ag/SnO<sub>2</sub"> 88/12 PW4 after annealing for 1 hr after 30% cold working[[File:Softening of Ag SnO2 88 12 PW4 after annealing.jpg|right|thumb|Softening of Ag/SnO₂ 88/12 PW4 after annealing for 1 hr after 30% cold working]]Fig. 2.93: Strain hardening of Ag/SnO₂ 98/2 PX by cold working[[File:Strain hardening of Ag SnO2 98 2 PX.jpg|right|thumb|Strain hardening of Ag/SnO₂ 98/2 PX by cold working]]Fig. 2.94: Softening of Ag/SnO₂ 98/2 PX after annealing for 1 hr after 80% cold working[[File:Softening of Ag SnO2 98 2 PX after annealing.jpg|right|thumb|Softening of Ag/SnO₂ 98/2 PX after annealing for 1 hr after 80% cold working]]Fig 2.95: Strain hardening of Ag/SnO₂ 92/8 PX by cold working[[File:Strain hardening of Ag SnO2 92 8 PX.jpg|right|thumb|Strain hardening of Ag/SnO₂ 92/8 PX by cold working]]Fig. 2.96: Softening of Ag/SnO₂ 92/8 PX after annealing for 1 hr after 40% cold working[[File:Softening of Ag SnO2 92 8 PX after annealing.jpg|right|thumb|Softening of Ag/SnO₂ 92/8 PX after annealing for 1 hr after 40% cold working]]Fig. 2.97: Strain hardening of internally oxidized Ag/SnO₂ 88/12 TOS F by cold working[[File:Strain hardening of internally oxidized Ag SnO2 88 12 TOS F.jpg|rightleft|thumb|Strain hardening of internally oxidized Ag/SnO<sub>2</subcaption> 88/12 TOS F by cold working]]Fig. 2.98: Softening of Ag/SnO₂ 88/12 TOS F after annealing for 1 hr after 30% cold working[[File:Softening of Ag SnO2 88 12 TOS F after annealing.jpg|right|thumb|Softening of Ag/SnO₂ 88/12 TOS F PW4 after annealing for 1 hr after 30% cold working]]Fig. 2.99: Strain hardening of internally oxidized Ag/SnO<sub>2</subcaption> 88/12P by cold working[[File:Strain hardening of internally oxidized Ag SnO2 88 12P.jpg|right|thumb|Strain hardening of internally oxidized Ag/SnO₂ 88/12P by cold working]]Fig. 2.100: Softening of Ag/SnO₂ 88/12P after annealing for 1 hr after 40% cold working[[File:Softening of Ag SnO2 88 12P after annealing.jpg|right|thumb|Softening of Ag/SnO<sub>2</subfigure>88/12P after annealing for 1 hr after 40% cold working]]Fig. 2.101: Strain hardening of Ag/SnO₂ 88/12 WPC by cold working[[File:Strain hardening of Ag SnO2 88 12 WPC.jpg|right|thumb|Strain hardening of Ag/SnO₂ 88/12 WPC by cold working]]Fig. 2.102: Softening of Ag/SnO₂ 88/12 WPC after annealing for 1 hr after different degrees of cold working[[File:Softening of Ag SnO2 88 12 WPC after annealing.jpg|right|thumb|Softening of Ag/SnO₂ 88/12 WPC after annealing for 1 hr after different degrees of cold working]]Fig. 2.103: Strain hardening of Ag/SnO₂ 86/14 WPC by cold working[[File:Strain hardening of Ag SnO2 86 14 WPC.jpg|right|thumb|Strain hardening of Ag/SnO₂ 86/14 WPC by cold working]]Fig. 2.104: Softening of Ag/SnO₂ 86/14 WPC after annealing for 1 hr after different degrees of cold working[[File:Softening of Ag SnO2 86 14 WPC.jpg|right|thumb|Softening of Ag/SnO₂ 86/14 WPC after annealing for 1 hr after different degrees of cold working]]Fig. 2.105: Strain hardening of Ag/SnO₂ 88/12 WPD by cold working[[File:Strain hardening of Ag SnO2 88 12 WPD.jpg|right|thumb|Strain hardening of Ag/SnO₂ 88/12 WPD by cold working]]Fig. 2.106: Softening of Ag/SnO₂ 88/12 WPD after annealing for 1 hr after different degrees of cold working[[File:Softening of Ag SnO2 88 12 WPD after annealing.jpg|right|thumb|Softening of Ag/SnO₂ 88/12 WPD after annealing for 1 hr after different degrees of cold working]]Fig. 2.108: Softening of Ag/SnO₂ 88/12 WPX after annealing for 1 hr after different degrees of cold working[[File:Softening of Ag SnO2 88 12 WPX.jpg|right|thumb|Softening of Ag/SnO₂ 88/12 WPX after annealing for 1 hr after different degrees of cold working]]Fig. 2.107: Strain hardening of Ag/SnO₂ 88/12 WPX by cold working[[File:Strain hardening of Ag SnO2 88 12 WPX.jpg|right|thumb|Strain hardening of Ag/SnO₂ 88/12 WPX by cold working]]Fig. 2.109: Micro structure of Ag/SnO₂ 92/8 PE: a) perpendicular to extrusion directionb) parallel to extrusion direction[[File:Micro structure of Ag SnO2 92 8 PE.jpg|right|thumb|Micro structure of Ag/SnO₂ 92/8 PE: a) perpendicular to extrusion direction b) parallel to extrusion direction]]Fig. 2.110: Micro structure of Ag/SnO₂ 88/12 PE: a) perpendicular to extrusion directionb) parallel to extrusion direction[[File:Micro structure of Ag SnO2 88 12 PE.jpg|right|thumb|Micro structure of Ag/SnO₂ 88/12 PE: a) perpendicular to extrusion direction b) parallel to extrusion direction]]Fig. 2.111: Micro structure of Ag/SnO₂ 88/12 PW: a) perpendicular to extrusion directionb) parallel to extrusion direction[[File:Micro structure of Ag SnO2 88 12 PW.jpg|right|thumb|Micro structure of Ag/SnO₂ 88/12 PW: a) perpendicular to extrusion direction b) parallel to extrusion direction]]Fig. 2.112: Micro structure of Ag/SnO₂ 98/2 PX: a) perpendicular to extrusion directionb) parallel to extrusion direction[[File:Micro structure of Ag SnO2 98 2 PX.jpg|right|thumb|Micro structure of Ag/SnO₂ 98/2 PX: a) perpendicular to extrusion direction b) parallel to extrusion direction]]Fig. 2.113: Micro structure of Ag/SnO₂ 92/8 PX: a) perpendicular to extrusion directionb) parallel to extrusion direction[[File:Micro structure of Ag SnO2 92 8PX.jpg|right|thumb|Micro structure of Ag/SnO₂ 92/8 PX: a) perpendicular to extrusion direction b) parallel to extrusion direction]]Fig. 2.114: Micro structure of Ag/SnO₂ 88/12 TOS F: a) perpendicular to extrusion directionb) parallel to extrusion direction[[File:Micro structure of Ag SnO2 88 12 TOS F.jpg|right|thumb|Micro structure of Ag/SnO₂ 88/12 TOS F: a) perpendicular to extrusion direction b) parallel to extrusion direction]]Fig. 2.115: Micro structure of Ag/SnO₂ 86/14 WPC: a) perpendicular to extrusion directionb) parallel to extrusion direction, 1) AgSnO₂ contact layer, 2) Ag backing layer[[File:Micro structure of Ag SnO2 86 14 WPC.jpg|right|thumb|Micro structure of Ag/SnO₂ 86/14 WPC: a) perpendicular to extrusion direction b) parallel to extrusion direction, 1) AgSnO2 contact layer, 2) Ag backing layer]]Fig. 2.116: Micro structure of Ag/SnO₂ 92/8 WTOS F: a) perpendicular to extrusion directionb) parallel to extrusion direction,1) AgSnO₂ contact layer, 2) Ag backing layer[[File:Micro structure of Ag SnO2 92 8 WTOS F.jpg|right|thumb|Micro structure of Ag/SnO₂ 92/8 WTOS F: a) perpendicular to extrusion direction b) parallel to extrusion direction,1) AgSnO2 contact layer, 2) Ag backing layer]]Fig. 2.117: Micro structure of Ag/SnO₂ 88/12 WPD: parallel to extrusion direction1) AgSnO₂ contact layer, 2) Ag backing layer[[File:Micro structure of Ag SnO2 88 12 WPD.jpg|right|thumb|Micro structure of Ag/SnO₂ 88/12 WPD: parallel to extrusion direction 1) AgSnO2 contact layer, 2) Ag backing layer]]Fig. 2.118: Micro structure of Ag/SnO₂ 88/12 WPX:parallel to extrusion direction1) AgSnO₂ contact layer, 2) Ag backing layer[[File:Micro structure of Ag SnO2 88 12 WPX.jpg|right|thumb|Micro structure of Ag/SnO₂ 88/12 WPX:parallel to extrusion direction 1) AgSnO2 contact layer, 2) Ag backing layer]]Fig. 2.119: Micro structure of Ag/SnO₂ 86/14 WPX: a) perpendicular to extrusion directionb) parallel to extrusion direction, 1) AgSnO₂ contact layer, 2) Ag backing layer[[File:Micro structure of Ag SnO2 86 14 WPX.jpg|right|thumb|Micro structure of Ag/SnO₂ 86/14 WPX: a) perpendicular to extrusion direction b) parallel to extrusion direction, 1) AgSnO2 contact layer, 2) Ag backing layer]]

'''Table 2.27<figure id="fig: Physical Properties Strain hardening of Powder Metallurgical Silver-Metal Oxide Materialsinternally oxidized Ag SnO2 88 12 TOS F"> with Fine Silver Backing Produced [[File:Strain hardening of internally oxidized Ag SnO2 88 12 TOS F.jpg|left|thumb|<caption>Strain hardening of internally oxidized Ag/SnO₂ 88/12 TOS F by the Press-Sinter-Repress Process'''cold working</caption>]]</figure> <table border="1" cellspacingfigure id="0" style="border-collapsefig:collapseSoftening of Ag SnO2 88 12 TOS F after annealing">[[File:Softening of Ag SnO2 88 12 TOS F after annealing.jpg|left|thumb|<trcaption>Softening of Ag/SnO<tdsub>2<p class="s11"/sub>Material88/12 TOS F after annealing for 1 hr after 30% cold working</caption>]]</pfigure> <p classfigure id="s11fig:Strain hardening of internally oxidized Ag SnO2 88 12P">DODUCO- Designation[[File:Strain hardening of internally oxidized Ag SnO2 88 12P.jpg|left|thumb|<caption>Strain hardening of internally oxidized Ag/SnO<sub>2</psub>88/12P by cold working</tdcaption>]]<td/figure> <p classfigure id="s11fig:Softening of Ag SnO2 88 12P after annealing">Additives[[File:Softening of Ag SnO2 88 12P after annealing.jpg|left|thumb|<caption>Softening of Ag/SnO<sub>2</psub>88/12 SP after annealing for 1 hr after 40% cold working</tdcaption>]]<td/figure> <p classfigure id="s11fig:Strain hardening of Ag SnO2 88 12 WPD">Density[[File:Strain hardening of Ag SnO2 88 12 WPD.jpg|left|thumb|<caption>Strain hardening of Ag/SnO₂ 88/12 WPD by cold working</caption>]]</pfigure> <p classfigure id="s11fig:Softening of Ag SnO2 88 12 WPD after annealing">[ g[File:Softening of Ag SnO2 88 12 WPD after annealing.jpg|left|thumb|<caption>Softening of Ag/SnO₂ 88/12 WPD after annealing for 1 hr after different degrees of cold working</caption>]]</cmfigure> <span classfigure id="s13fig:Micro structure of Ag SnO2 92 8 PE">3[[File:Micro structure of Ag SnO2 92 8 PE.jpg|left|thumb|<caption>Micro structure of Ag/spanSnO<sub>]2</psub>92/8 PE: a) perpendicular to extrusion direction b) parallel to extrusion direction</tdcaption>]]<td/figure> <p classfigure id="s11fig:Micro structure of Ag SnO2 88 12 PE">Electrical[[File:Micro structure of Ag SnO2 88 12 PE.jpg|left|thumb|<caption>Micro structure of Ag/SnO<sub>2</psub>88/12 PE: a) perpendicular to extrusion direction b) parallel to extrusion direction<p class="s11"/caption>Resistivity]]</pfigure> <p classfigure id="s11fig:Micro structure of Ag SnO2 88 12 PW">[µ[File:Micro structure of Ag SnO2 88 12 PW.jpg|left|thumb|<caption>Micro structure of Ag/SnO₂ 88/12 SPW: a) perpendicular to extrusion direction b) parallel to extrusion direction</caption>]]</figure> <span classfigure id="s14fig:Micro structure of Ag SnO2 88 12 TOS F">S ·[[File:Micro structure of Ag SnO2 88 12 TOS F.jpg|left|thumb|<caption>Micro structure of Ag/spanSnO<sub>cm]2</psub>88/12 TOS F: a) perpendicular to extrusion direction b) parallel to extrusion direction</tdcaption>]]<td/figure> <p classfigure id="s11fig:Micro structure of Ag SnO2 92 8 WTOS F">Electrical[[File:Micro structure of Ag SnO2 92 8 WTOS F.jpg|left|thumb|<caption>Micro structure of Ag/p>SnO<p class="s11"sub>Conductivity2</psub>92/8 WTOS F: a) perpendicular to extrusion direction b) parallel to extrusion direction,1) AgSnO2 contact layer, 2) Ag backing layer</tdcaption>]]<td/figure> <p classfigure id="s11fig:Micro structure of Ag SnO2 88 12 WPD">Vickers[[File:Micro structure of Ag SnO2 88 12 WPD.jpg|left|thumb|<caption>Micro structure of Ag/SnO₂ 88/12 WPD: parallel to extrusion direction 1) AgSnO2 contact layer, 2) Ag backing layer</caption>]]</pfigure> <p div class="s11clear">Hardness</pdiv>  <p classfigtable id="s11tab:Physical Properties of Powder Metallurgical Silver-Metal Oxide Materials with Fine Silver Backing Produced by the Press-Sinter-Repress Process">HV 10<caption>'''<!--Table 2.</p27:-->Physical Properties of Powder Metallurgical Silver-Metal Oxide Materials with Fine Silver Backing Produced by the Press-Sinter-Repress Process'''</tdcaption></trtable class="twocolortable"><tr><tdth rowspan="2"><p class="s11">Material/</p><p class="s11">DODUCO- Designation</p></tdth><tdth rowspan="2"><p class="s11">Additives</p></tdth><tdth rowspan="2"><p class="s11">Density</p><p class="s11">[ g/cm<span class="s13"sup>3</spansup>]</p></tdth><tdth rowspan="2"><p class="s11">Electrical</p><p class="s11">Resistivity</p><p class="s11">[µ<span class="s14">S ·</span>cm]</p></tdth><tdth colspan="2"><p class="s11">[% IACS]Electrical</p></td><td><p class="s11">[MS/m]Conductivity</p></tdth><tdth rowspan="2"><p class="s11">Vickers</p><p class="s11">Hardness</p><p class="s11">HV 10.</p></tdth></tr><tr><th><p class="s11">[%IACS]</p></th><th><p>[MS/m]</p></th></tr><tr><td><p class="s11">AgCdO 90/10EP10</p><p class="s11">DODURIT CdO 10EP</p></td><td/><td><p class="s11">10.1</p></td><td><p class="s11">2.08</p></td><td><p class="s12">83</p></td><td><p class="s12">48</p></td><td><p class="s11">60</p></td></tr><tr><td><p class="s11">AgCdO 85/15 EP DODURIT CdO 15EP</p></td><td/><td><p class="s11">9.9</p></td><td><p class="s11">2.27</p></td><td><p class="s12">76</p></td><td><p class="s12">44</p></td><td><p class="s11">65</p></td></tr><tr><td><p class="s11">AgSnO² AgSnO₂ 90/10 EPX SISTADOX 10EPX</p></td><td><p class="s11">CuO and</p><p class="s11">Bi² O³Bi₂ O₃</p></td><td><p class="s11">9.8</p></td><td><p class="s11">2.22</p></td><td><p class="s12">78</p></td><td><p class="s12">45</p></td><td><p class="s11">55</p></td></tr><tr><td><p class="s11">AgSnO² AgSnO₂ 88/12EPX SISTADOX 12EPX12</p></td><td><p class="s11">CuO and</p><p class="s11">Bi² O³Bi₂ O₃</p></td><td><p class="s11">9.6</p></td><td><p class="s11">2.63</p></td><td><p class="s12">66</p></td><td><p class="s12">38</p></td><td><p class="s11">60</p></td></tr></table>

*'''Silver–zinc oxide (DODURIT ZnO) materials'''Silver zinc oxide (DODURIT ZnO) contact materials with mostly 6 - 10 wt% oxide content , including other small metal oxides , are produced exclusively by powder metallurgy ''[[#figures1|(Figs. 2.120 58 – 2.12563)'' '']]<!--(Table 2.28)''-->. Adding WO₃ or Ag₂WO₄ in the process b) - as described in the preceding chapter on Ag/SnO₂ - has proven most effective for applications in AC relays, wiring devices, and appliance controls. Just like with the other Ag metal oxide materials, semi-finished materials in strip and wire form are used to manufacture contact tips and rivets. Because of their high resistance against welding and arc erosion Ag/ZnO materials present an economic alternative to Cd free Ag-tin oxide contact materials ''(Tables <xr id="tab:Contact and Switching Properties of Silver–Metal Oxide Materials"/><!--(Tab. 2.30 )--> and <xr id="tab:Application Examples of Silver–Metal Oxide Materials"/>)<!--(Tab. 2.31)''-->.

Fig. 2.120: Strain hardening of Ag/ZnO 92/8 PW25 by cold working[[File:Strain hardening of Ag ZnO 92 8 PW25.jpg|right|thumb|Strain hardening of Ag/ZnO 92/8 PW25 by cold working]]Fig. 2.121: Softening of Ag/ZnO 92/8 PW25 after annealing for 1 hr after 30% cold working[[File:Softening of Ag ZnO 92 8 PW25.jpg|right|thumb|Softening of Ag/ZnO 92/8 PW25 after annealing for 1 hr after 30% cold working]]Fig. 2.122: Strain hardening of Ag/ZnO 92/8 WPW25 by cold working[[File:Strain hardening of Ag ZnO 92 8 WPW25.jpg|right|thumb|Strain hardening of Ag/ZnO 92/8 WPW25 by cold working]]Fig. 2.123: Softening of Ag/ZnO 92/8 WPW25 after annealing for 1hr after different degrees of cold working[[File:Softening of Ag ZnO 92 8 WPW25.jpg|right|thumb|Softening of Ag/ZnO 92/8 WPW25 after annealing for 1hr after different degrees of cold working]]Fig. 2.115 oder 2.124: Micro structure of Ag/ZnO 92/8 Pw25: a) perpendicular to extrusion directionb) parallel to extrusion direction[[File<figtable id="tab:Micro structure of Ag ZnO 92 8 Pw25tab2.jpg|right|thumb|Micro structure of Ag/ZnO 92/8 Pw25: a) perpendicular to extrusion direction b) parallel to extrusion direction]]28">Fig. 2.116 oder <caption>'''<!--Table 2.125: Micro structure of Ag/ZnO 92/8 WPW25:a) perpendicular to extrusion directionb) parallel to extrusion direction, 1) Ag/ZnO contact layer, 2) Ag backing layer[[File28:Micro structure --> Physical and Mechanical Properties as well as Manufacturing Processes and Forms of Ag ZnO 92 8 WPW25.jpg|right|thumb|Micro structure Supply of Ag/ZnO 92/8 WPW25:a) perpendicular to extrusion direction b) parallel to extrusion direction, 1) AgExtruded Silver-Zinc Oxide Contact'''</ZnO contact layer, 2) Ag backing layer]]caption>

'''Table 2.29: Optimizing of Silver–Tin Oxide Materials Regarding their Switching Properties and Forming Behavior'''<table border{| class="1" cellspacing="0twocolortable" style="bordertext-align: left; font-collapsesize:collapse12px"><tr><td><p class="s12">|-!Material/!Silver Content<br /p>[wt%]!Additives!Density<p class="s12">Material Group<br /p><[g/td>cm<tdsup><p class="s12">Special Properties3</psup>]!Electrical<br /td>Resistivity<br /tr><tr><td><p class[μΩ·cm]!colspan="s122">Ag/SnO<span classstyle="s48text-align:center">2 |Electrical<br /span>PEConductivity<br /p>[% IACS] [MS/m]!Vickers<br /td>Hardness<tdbr />Hv1!Tensile<p class="s12">Especially suitable for automotive relays<br /p>Strength<p class="s12">(lamp loads)<br /p>[MPa]!Elongation<br /td><td><p class="s12">Good formability (contact rivetssoft annealed)<br /p>A[%]min.!Manufacturing<br /td>Process!Form of<br /tr><tr><td><p class="s12">Supply|-|Ag/SnO<span class="s48">2 ZnO 92/8P<br /span>98/|91 - 93||9.8|2 PX/PC.22|78|45|60 - 95|220 - 350|25|Powder Metallurgy<br /p><a) indiv. powders|1|-|Ag/td><td><p class="s12">Especially good heat resistance<ZnO 92/p>8PW25<br /td><td><p class="s12">Easily riveted, can be directly welded</p></td></tr><tr><td><p class="s12">|91 - 93|Ag/SnO<span class="s48"sub>2 </spansub>TOS FWO</psub>4</td><td><p class="s12">Especially suited for high inductive</p><p class="s12">DC loads</psub>|9.6|2.08|83|48|65 - 105|230 - 340|25|Powder Metallurgy<br /td><td><p class="s12">Very good formability (contact rivetsc)<coated|1|-|Ag/p><ZnO 90/td>10PW25<br /tr><tr><td><p class="s12">|89 - 91|Ag/SnO<span class="s48"sub>2 </spansub>WPCWO</psub>4</tdsub><td><p class="s12">For AC|9.6|2.17|79|46|65 -3 and AC100|230 -4 applications in motor350|20|Powder Metallurgy<br /p><p class="s12">switches (contactorsc)<coated|1|-|Ag/p><ZnO 92/td>8WP<tdbr />|91 - 93||9.8|2.0|86|50|60 - 95|||Powder Metallurgy<br /tr><tr><td><p class="s12">with Ag/SnO<span class="s48">backing a) individ.|2 <|-|Ag/span>WPD<ZnO 92/p>8WPW25<br /td><td><p class="s12">Especially suited for severe loads (AC|91 -4)</p><p class="s12">and high switching currents</p></td><td/></tr><tr><td><p class="s12">93|Ag/SnO<span class="s48"sub>2 </spansub>WPXWO</psub>4</tdsub><td><p class="s12">For standard motor loads (AC|9.6|2.08|83|48|65 -3) and105|||Powder Metallurgy<br /p><p class="s12">Resistive loads (AC-1c), DC loads (DCcoated|2|-5)<|Ag/ZnO 90/p>10WPW25<br /td>|89 - 91|Ag<td/sub>2</trsub>WO<tr><tdsub>4<p class="s12">Ag/SnO<span class="s48"sub>|9.6|2 .7|79|46|65 - 110|||Powder Metallurgy<br /span>WTOSFc) coated|2|}</pfigtable></td><td><p class 1 ="s12">Especially suitable for high inductive DC</p><p classWires, Rods, Contact rivets, 2 ="s12">loads</p></td><td/></tr></table>Strips, Profiles, Contact tips

'''Table 2.31: Application Examples of Silver–Metal Oxide Materials'''<table border="1" cellspacing="0" stylediv class="bordermultiple-collapse:collapseimages"><tr><td><p classfigure id="s12">Material</p></td><td><p class="s12">Application Examples</p></td></tr><tr><td><p class="s12">fig:Strain hardening of Ag/CdO</p></td><td><p class="s12">Micro switches, Network relays, Wiring devices, Appliance switches, Main switches, contactors, Small (main) power switches</p></td></tr><tr><td><p class="s12ZnO 92 8 PW25">[[File:Strain hardening of Ag/SnOZnO 92 8 PW25.jpg|left|thumb|<span class="s48">2</span></p></td><td><p class="s12">Micro switches, Network relays, Automotive relays, Appliance switches,</p><p class="s12">Main switches, contactors, Fault current protection relays (paired against</p><p class="s12">Ag/C), (Main) Power switches</p></td></tr><tr><td><p class="s12"caption>Strain hardening of Ag/ZnO<92/p>8 PW25 by cold working</td><td><p class="s12">Wiring devices, AC relays, Appliance switches, Motor-protective circuit</p><p class="s12">breakers (paired with Ag/Ni or Ag/C), Fault current circuit breakers paired againct Ag/C, (Main) Power switches</p></td></trcaption>]]</tablefigure>

<figure id====Silver–Graphite (GRAPHOR)-Materials===="fig:Softening of Ag ZnO 92 8 PW25"> [[File:Softening of Ag ZnO 92 8 PW25.jpg|left|thumb|<caption>Softening of Ag/C (GRAPHOR) contact materials are usually produced by powder metallurgy with graphite contents of 2 – 5 wtZnO 92/8 PW25 after annealing for 1 hr after 30% ''(Table 2.32)''. The earlier typicalcold working</caption>]]manufacturing process of single pressed tips by pressing - sintering - repressing (PSR) has been replaced in Europe for quite some time by extrusion. In North America and some other regions however the PSR process is still used to some extend mainly for cost reasons.</figure>

The extrusion <figure id="fig:Strain hardening of sintered billets is now the dominant manufacturing method for semi-finished AgC materials ''(Figs. 2.126 – 2.129)''. The hot extrusion process results in a high density material with graphite particles stretched and oriented in the extrusion direction ''(Figs. 2.130 – 2.133)''. Depending on the extrusion method in either rod or strip form the graphite particles can be oriented in the finished contact tips perpendicular (GRAPHOR) or parallel (GRAPHOR D) to the switching contact surface ''(Figs. 2.131 and 2.132)''Ag ZnO 92 8 WPW25"> [[File:Strain hardening of Ag ZnO 92 8 WPW25.jpg|left|thumb|<caption>Strain hardening of Ag/ZnO 92/8 WPW25 by cold working</caption>]]</figure>

Since the graphite particles in the <figure id="fig:Softening of Ag matrix ZnO 92 8 WPW25"> [[File:Softening of Ag/C materials prevent contact tips from directly being welded or brazed, a graphite free bottom layer is requiredZnO 92 8 WPW25. This is achieved by either burning out (de-graphitizing) the graphite selectively on one side jpg|left|thumb|<caption>Softening of the tips or by compound extrusion Ag/ZnO 92/8 WPW25 after annealing for 1hr after different degrees of a Agcold working</caption>]]</C billet covered with a fine silver shell.figure>

<figure id="fig:Micro structure of Ag ZnO 92 8 PW25"> [[File:Micro structure of Ag ZnO 92 8 Pw25.jpg|left|thumb|<caption>Micro structure of Ag/C contact materials exhibit on the one hand an extremely high resistance ZnO 92/8 PW25: a) perpendicular to contact welding but on the other have a low arc erosion resistance. This is caused by the reaction of graphite with the oxygen in the surrounding atmosphere at the high temperatures created by the arcing. The weld resistanceis especially high for materials with the graphite particle orientation extrusion direction b) parallel to the arcing contact surface. Since the contact surface after arcing consists of pure silver the contact resistance stays consistently low during the electrical life of the contact parts.extrusion direction</caption>]]</figure>

A disadvantage <figure id="fig:Micro structure of the AgZnO 92 8 WPW25"> [[File:Micro structure of Ag ZnO 92 8 WPW25.jpg|right|thumb|<caption>Micro structure of Ag/ZnO 92/C materials is their rather high erosion rate. In materials with 8 WPW25:a) perpendicular to extrusion direction b) parallel graphite orientation this can be improved if part of the graphite is incorporated into the material in the form of fibers (GRAPHOR DFto extrusion direction, 1)Ag/ZnO contact layer, ''(Fig. 2.133)''. The weld resistance is determined by the total content of graphite particles.Ag backing layer</caption>]]</figure></div><div class="clear"></div>

<figtable id="tab:tab2.29"><caption>'''<!--Table 2.29:-->Optimizing of Silver–Tin Oxide Materials Regarding their Switching Properties and Forming Behavior'''</caption><table class="twocolortable"><tr><th><p class="s12">Material/</p><p class="s12">Material Group</p></th><th><p class="s12">Special Properties<th colspan="2"></p></th></tr><tr><td><p class="s12">Ag/SnO₂ PE</p></td><td><p class="s12">Especially suitable for automotive relays</p><p class="s12">(lamp loads)</p></td><td><p class="s12">Good formability (contact rivets)</p></td></tr><tr><td><p class="s12">Ag/SnO₂ TOS F</p></td><td><p class="s12">Especially suited for high inductive</p><p class="s12">DC loads</p></td><td><p class="s12">Very good formability (contact rivets)</p></td></tr><tr><td><p class="s12">Ag/SnO₂ WPD</p></td><td><p class="s12">Especially suited for severe loads (AC-4)</p><p class="s12">and high switching currents</p></td><td/></tr><tr><td><p class="s12">Ag/SnO₂ W TOS F</p></td><td><p class="s12">Especially suitable for high inductive DC</p><p class="s12">loads</p></td><td/></tr></table></figtable>  <figtable id="tab:Contact and Switching Properties of Silver–Metal Oxide Materials"><caption>'''<!--Table 2.30:-->Contact and Switching Properties of Silver–Metal Oxide Materials'''</caption> {| class="twocolortable" style="text-align: left; font-size: 12px"|-!Material!Properties|-|Ag/SnO₂<br />|Environmentally friendly materials,<br />Very high resistance against welding during current-on-switching,<br />Weld resistance increases with higher oxide contents,<br />Low and stable contact resistance over the life of the device and good<br />temperature rise properties through use of special additives,<br />High arc erosion resistance and contact life,<br />Very low and flat material transfer during DC load switching,<br />Good arc moving and very good arc extinguishing properties|-|Ag/ZnO<br />|Environmentally friendly materials,<br />High resistance against welding during current-on-switching<br />(capacitor contactors),<br />Low and stable contact resistance through special oxide additives,<br />Very high arc erosion resistance at high switching currents,<br />Less favorable than Ag/SnO₂ for electrical life and material transfer,<br />With Ag₂WO₄ additive especially suitable for AC relays|}</figtable>  <figtable id="tab:Application Examples of Silver–Metal Oxide Materials"><caption>'''<!--Table 2.31:-->Application Examples of Silver–Metal Oxide Materials'''</caption><table class="twocolortable"><tr><th><p class="s12">Material</p></th><th><p class="s12">Application Examples</p></th></tr><tr><td><p class="s12">Ag/SnO₂<span class="s48"></span></p></td><td><p class="s12">Micro switches, Network relays, Automotive relays, Appliance switches,</p><p class="s12">Main switches, contactors, Fault current protection relays (paired against</p><p class="s12">Ag/C), (Main) Power switches</p></td></tr><tr><td><p class="s12">Ag/ZnO</p></td><td><p class="s12">Wiring devices, AC relays, Appliance switches, Motor-protective circuit</p><p class="s12">breakers (paired with Ag/Ni or Ag/C), Fault current circuit breakers paired againct Ag/C, (Main) Power switches</p></td></tr></table></figtable> ====Silver–Graphite Materials====Ag/C contact materials are usually produced by powder metallurgy with graphite contents of 2 – 6 wt% (<xr id="tab:tab2.32"/>)<!--(Table 2.32)-->. The earlier typical manufacturing process of single pressed tips by pressing - sintering - repressing (PSR) has been replaced in Europe for quite some time by extrusion. In North America and some other regions however the PSR process is still used to some extend mainly for cost reasons. The extrusion of sintered billets is now the dominant manufacturing method for semi-finished AgC materials<!--[[#figures3|(Figs. 64 – 67)]]<!--(Figs. 2.126 – 2.129)-->. The hot extrusion process results in a high density material with graphite particles stretched and oriented in the extrusion direction [[#figures4|(Figs. 68 – 71)]]<!--(Figs. 2.130 – 2.133)-->. Depending on the extrusion method in either rod or strip form, the graphite particles can be oriented in the finished contact tips perpendicular or parallel to the switching contact surface (<xr id="fig:Micro structure of Ag C 95 5"/><!--(Fig. 2.131)--> and <xr id="fig:Micro structure of Ag C 96 4 D"/>)<!--(Fig. 2.132)-->. Since the graphite particles in the Ag matrix of Ag/C materials prevent contact tips from directly being welded or brazed, a graphite free bottom layer is required. This is achieved by burning out (de-graphitizing) the graphite selectively on one side of the tips. Ag/C contact materials exhibit on the one hand an extremely high resistance to contact welding but on the other have a low arc erosion resistance. This is caused by the reaction of graphite with the oxygen in the surrounding atmosphere at the high temperatures created by the arcing. The weld resistance is especially high for materials with the graphite particle orientation parallel to the arcing contact surface. Since the contact surface after arcing consists of pure silver, the contact resistance stays consistantly low during the electrical life of the contact parts. A disadvantage of the Ag/C materials is their rather high erosion rate. In materials with parallel graphite orientation this can be improved, if a part of the graphite is incorporated into the material (Ag/C DF) in the form of fibers (<xr id="fig:Micro structure of Ag C DF"/>)<!--(Fig. 2.133)-->. The weld resistance is determined by the total content of graphite particles. Ag/C tips with vertical graphite particle orientation are produced in a specific sequence: Extrusion to rods, cutting of double thickness tips, burning out of graphite to a controlled layer thickness, and a second cutting to single tips. Such contact tips are especially well suited for applications which require both, a high weld resistance and a sufficiently high arc erosion resistance (<xr id="tab:tab2.33"/>)<!--(Table 2.33)-->. For attachment of Ag/C tips welding and brazing techniques are applied. Welding the actual process depends on the material's graphite orientation. For Ag/C tips with vertical graphite orientation the contacts are assembled with single tips. For parallel orientation a more economical attachment starting with contact material in strip or profile tape form is used in integrated stamping and welding operations with the tape fed into the weld station, cut off to tip form and then welded to the carrier material before forming the final contact assembly part. For special low energy welding , the Ag/C profile tapes GRAPHOR D and DF can be pre-coated with a thin layer of high temperature brazing alloys such as CuAgP.

The main applications for Ag/C materials are protective switching devices such as miniature molded case circuit breakers, motor-protective circuit breakers, and fault current circuit breakers, where during short circuit failures , highest resistance against welding is required ''(<xr id="tab:tab2.34"/>)<!--(Table 2.34)''-->. For higher currents the low arc erosion resistance of Ag/C is compensated by asymmetrical pairing with more erosion resistant materials such as Ag/Ni , Ag/W and Ag/WWC. <div class="multiple-images"><figure id="fig:Strain hardening of Ag C 96 4 D">[[File:Strain hardening of Ag C 96 4 D.jpg|left|thumb|<caption>Strain hardening of Ag/C 96/4 by cold working</caption>]]</figure> <figure id="fig:Softening of Ag C 96 4 D"> [[File:Softening of Ag C 96 4 D.jpg|left|thumb|<caption>Softening of Ag/C 96/4 after annealing</caption>]]</figure> <figure id="fig:Strain hardening of Ag C DF"> [[File:Strain hardening of Ag C DF.jpg|left|thumb|<caption>Strain hardening of Ag/C DF by cold working</caption>]]</figure> <figure id="fig:Softening of Ag C DF after annealing"> [[File:Softening of Ag C DF after annealing.jpg|left|thumb|<caption>Softening of Ag/C DF after annealing</caption>]]</figure> <figure id="fig:Micro structure of Ag C 97 3"> [[File:Micro structure of Ag C 97 3.jpg|left|thumb|<caption>Micro structure of Ag/C 97/3: a) perpendicular to extrusion direction b) parallel to extrusion direction, 1) Ag/C contact layer, 2) Ag backing layer</caption>]]</figure>

Fig. 2.126<figure id="fig: Strain hardening Micro structure of Ag/C 96/4 D by cold working95 5"> [[File:Strain hardening Micro structure of Ag C 96 4 D95 5.jpg|rightleft|thumb|Strain hardening <caption>Micro structure of Ag/C 9695/5: a) perpendicular to extrusion direction b) parallel to extrusion direction, 1) Ag/C contact layer, 2) Ag backing layer</4 D by cold workingcaption>]]</figure>

Fig. 2.127<figure id="fig: Softening Micro structure of Ag/C 96/4 D after annealing"> [[File:Softening Micro structure of Ag C 96 4 D.jpg|rightleft|thumb|Softening <caption>Micro structure of Ag/C 96/4 D after annealing: a) perpendicular to extrusion direction b) parallel to extrusion direction, 1) Ag/C contact layer, 2) Ag backing layer</caption>]]</figure>

Fig. 2.128<figure id="fig: Strain hardening Micro structure of Ag/C DF by cold working"> [[File:Strain hardening Micro structure of Ag C DF.jpg|rightleft|thumb|Strain hardening <caption>Micro structure of Ag/C DF by cold working: a) perpendicular to extrusion direction b) parallel to extrusion direction, 1) Ag/C contact layer, 2) Ag/Ni 90/10 backing layer</caption>]]</figure></div><div class="clear"></div>

Fig<figtable id="tab:tab2. 32"><caption>'''<!--Table 2.129: Softening of Ag/C DF after annealing[[File32:Softening of Ag C DF after annealing.jpg|right|thumb|Softening -->Physical Properties of AgSilver–Graphite Contact Materials'''</C DF after annealing]]caption>

Fig. 2.130{| class="twocolortable" style="text-align: left; font-size: Micro structure of Ag12px"|-!Material !Silver Content<br />[wt%]!Density<br /C 97>[g/cm³]!Melting Point<br />[°C]!Electrical Resistivity<br />[μΩ·cm]!colspan="2" style="text-align: a) perpendicular to extrusion directioncenter"|Electrical<br />Conductivity<br />[% IACS] [MS/m]!Vickers-Hardnes<br />HV10<br />42 - 45|-b) parallel to extrusion direction, 1) |Ag/C contact layer, 98/2) Ag backing layer[[File:Micro structure of Ag C |97 3.jpg5 - 98.5|9.5|960|1.85 - 1.92|right90 - 93|48 - 50|thumb42 - 44|-|Micro structure of Ag/C 97/3: a) perpendicular to extrusion direction b) parallel to extrusion direction, |96.5 - 97.5|9.1|960|1) .92 - 2.0|86 - 90|45 - 48|41 - 43|-|Ag/C contact layer, 96/4|95.5 - 96.5|8.7|960|2.04 - 2) .13|81 - 84|42 - 46|40 - 42|-|Ag backing layer/C 95/5|94.5 - 95.5|8.5|960|2.12 - 2.22|78 - 81|40 - 44|40 - 60|-|AgC DF<br />GRAPHOR DF[[#text-reference1|¹]]|95.7 - 96.7|8.7 - 8.9|960|2.27 - 2.50|69 - 76|40 - 44|-|}<div id="text-reference1">₁ Graphite content 3.8 wt%, Graphite particles and fibers parallel to switching surface</div></figtable>

<figtable id="tab:tab2.33"><caption>'''<!--Table 2.3233: Physical Properties -->Contact and Switching properties of Silver–Graphite (GRAPHOR) Contact Materials'''</caption><table class="twocolortable"><tr><th><p class="s12">Material</p></p></th><th><p class="s11">Properties</p></th></tr><tr><td><p class="s12">Ag/C</p></p></td><td><p class="s12">Highest resistance against welding during make operations at high currents,</p><p class="s12">High resistance against welding of closed contacts during short circuit,</p><p class="s12">Increase of weld resistance with higher graphite contents, Low contact resistance,</p><p class="s12">Low arc erosion resistance, especially during break operations, Higher arc erosion with increasing graphite contents, at the same time carbon build-up on switching chamber walls increases, silver-graphite with vertical orientation has better arc erosion resistance, parallel orientation has better weld resistance,</p><p class="s12">Limited arc moving properties, therefore paired with other materials,</p><p class="s12">Limited formability,</p><p class="s12">Can be welded and brazed with decarbonized backing, GRAPHOR DF is optimized for arc erosion resistance and weld resistance</p></td></tr></table></figtable>

<figtable id="tab:tab2.34"><caption>'''<!--Table 2.34: -->Application Examples and Forms of Supply of Silver– Graphite (GRAPHOR) Contact Materials'''</caption><table borderclass="1" cellspacing="0" style="border-collapse:collapsetwocolortable"><tr><tdth><p class="s12">Material/</p><p class="s12">DODUCO Designation</p></tdth><tdth><p class="s12">Application Examples</p></tdth><tdth><p class="s12">Form of Supply</p></tdth></tr><tr><td><p class="s12">Ag/C 98/2</p><p class="s12">GRAPHOR 2</p></td><td><p class="s12">Motor circuit breakers, paired with Ag/Ni</p></td><td><p class="s12">Contact tips, brazed and welded contact parts, some contact rivets</p><p class="s12">Contact profiles (weld tapes), Contact tips, brazed and welded contact parts</p></td></tr><tr><td><p class="s12">Ag/C 97/3</p><p class="s12">GRAPHOR 3</p><p class="s12">Ag/C 96/4</p><p class="s12">GRAPHOR 4</p><p class="s12">Ag/C 95/5</p><p class="s12">GRAPHOR 5</p><p class="s12">GRAPHOR 3D GRAPHOR 4D GRAPHOR Ag/C DF</p></td><td><p class="s12">Circuit breakers, paired with Cu, Motor-protective circuit breakers, paired with Ag/Ni,</p><p class="s12">Fault current circuit breakers, paired with Ag/Ni, Ag/W, Ag/WC, Ag/SnO₂<span class="s45">2</span>, Ag/ZnO,</p><p class="s12">(Main) Power switches, paired with Ag/Ni, Ag/W</p></td><td><p class="s12">Contact tips, brazed and welded contact</p><p class="s12">parts, some contact rivets with</p><p class="s12">Ag/C97/3</p></td></tr><tr><td><p class="s12">Ag/C 97/3</ptable><p class="s12">GRAPHOR 3</p><p class="s12">Ag/C 96/4</p><p class="s12">GRAPHOR 4</p><p class="s12">Ag/C 95/5</p><p class="s12">GRAPHOR 5</p><p class="s12">GRAPHOR 3D GRAPHOR 4D GRAPHOR DF</p></td><td><p class="s12">Circuit breakers, paired with Cu, Motor-protective circuit breakers, paired with Ag/Ni,</p><p class="s12">Fault current circuit breakers, paired with Ag/Ni, Ag/W, Ag/WC, Ag/SnO<span class="s45">2</span>, Ag/ZnO,</p><p class="s12">(Main) Power switches, paired with Ag/Ni, Ag/W</p></td><td><p class="s12">Contact profiles (weld tapes), Contact tips, brazed and welded contact parts</p></td></tr><tr><td/><td/></tr></tablefigtable>