→Silver-Metal Oxide Materials Ag/CdO, Ag/SnO2, Ag/ZnO
Over the past years, many Ag/CdO contact materials have been replaced by Ag/SnO<sub>2</sub> based materials with 2-14 wt% SnO<sub>2</sub> because of the toxicity of Cadmium. This changeover was further favored by the fact that Ag/SnO<sub>2</sub> contacts quite often show improved contact and switching properties such as lower arc erosion, higher weld resistance, and a significant lower tendency towards material transfer in DC switching circuits <xr id="tab:tab2.30"/><!--(Table 2.30)-->. Ag/SnO<sub>2</sub> materials have been optimized for a broad range of applications by other metal oxide additives and modification in the manufacturing processes that result in different metallurgical, physical and electrical properties<xr id="tab:tab2.28"/><!--(Tab. 2.28)--> und <xr id="tab:tab2.29"/><!--(Table 2.29)-->.
Manufacturing of Ag/SnO<sub>2</sub> by ''internal oxidation'' is possible in principle, but during heat treatment of alloys containing > 5 wt% of tin in oxygen, dense oxide layers formed on the surface of the material prohibit the further diffusion of oxygen into the bulk of the material. By adding Indium or Bismuth to the alloy the internal oxidation is possible and results in materials that typically are rather hard and brittle and may show somewhat elevated contact resistance and is limited to applications in relays. To make a ductile material with fine oxide dispersion (SISTADOX TOS F) <xr id="fig:Micro structure of Ag SnO2 88 12 TOS F"/><!--(Fig. 2.114)--> it is necessary to use special process variations in oxidation and extrusion which lead to materials with improved properties in relays. Adding a brazable fine silver layer to such materials results in a semifinished material suitable for the manufacture as smaller weld profiles (SISTADOX WTOS F) <xr id="fig:Micro structure of Ag SnO2 92 8 WTOS F"/><!--(Fig. 2.116)-->. Because of their resistance to material transfer and low arc erosion these materials find for example a broader application in automotive relays <xr id="tab:tab2.31Application Examples of Silver–Metal Oxide Materials"/><!--(Table 2.31)-->.