→Silver–Graphite (GRAPHOR)-Materials
<div id="figures3">
<xr id="fig:fig2.126Strain hardening of Ag C 96 4 D"/> Fig. 2.126: Strain hardening of Ag/C 96/4 D by cold working
<xr id="fig:fig2.127Softening of Ag C 96 4 D"/> Fig. 2.127: Softening of Ag/C 96/4 D after annealing
<xr id="fig:fig2.128Strain hardening of Ag C DF"/> Fig. 2.128: Strain hardening of Ag/C DF by cold working
<xr id="fig:fig2.129Softening of Ag C DF after annealing"/> Fig. 2.129: Softening of Ag/C DF after annealing
</div>
<div id="figures4">
<xr id="fig:fig2.130Micro structure of Ag C 97 3"/> Fig. 2.130: Micro structure of Ag/C 97/3: a) perpendicular to extrusion direction
b) parallel to extrusion direction, 1) Ag/C contact layer, 2) Ag backing layer
<div class="multiple-images">
<figure id="fig:fig2.126Strain hardening of Ag C 96 4 D">
[[File:Strain hardening of Ag C 96 4 D.jpg|left|thumb|<caption>Strain hardening of Ag/C 96/4 D by cold working</caption>]]
</figure>
<figure id="fig:fig2.127Softening of Ag C 96 4 D">
[[File:Softening of Ag C 96 4 D.jpg|left|thumb|<caption>Softening of Ag/C 96/4 D after annealing</caption>]]
</figure>
<figure id="fig:fig2.128Strain hardening of Ag C DF">
[[File:Strain hardening of Ag C DF.jpg|left|thumb|<caption>Strain hardening of Ag/C DF by cold working</caption>]]
</figure>
<figure id="fig:fig2.129Softening of Ag C DF after annealing">
[[File:Softening of Ag C DF after annealing.jpg|left|thumb|<caption>Softening of Ag/C DF after annealing</caption>]]
</figure>
<figure id="fig:fig2.130Micro structure of Ag C 97 3">
[[File:Micro structure of Ag C 97 3.jpg|left|thumb|<caption>Micro structure of Ag/C 97/3: a) perpendicular to extrusion direction b) parallel to extrusion direction, 1) Ag/C contact layer, 2) Ag backing layer</caption>]]
</figure>