→Silver-Nickel (SINIDUR) Materials
</figtable>
<xr id="fig:fig2.71"/> Fig. 2.71: Strain hardening of Ag/Ni 90/10 by cold working <xr id="fig:fig2.72"/> Fig. 2.72: Softening of Ag/Ni 90/10 after annealing for 1 hr after 80% cold working <xr id="fig:fig2.73"/> Fig. 2.73: Strain hardening of Ag/Ni 80/20 by cold working <xr id="fig:fig2.74"/> Fig. 2.74: Softening of Ag/Ni 80/20 after annealing for 1 hr after 80% cold working <xr id="fig:fig2.75"/> Fig. 2.75: Micro structure of Ag/Ni 90/10 a) perpendicular to the extrusion direction b) parallel to the extrusion direction <xr id="fig:fig2.76"/> Fig. 2.76: Micro structure of Ag/Ni 80/20 a) perpendicular to the extrusion direction b) parallel t o the extrusion direction <div class="multiple-images"><figure id="fig:fig2.71">
[[File:Strain hardening of AgNi9010 by cold working.jpg|right|thumb|Strain hardening of Ag/Ni 90/10 by cold working]]
[[File:Softening of AgNi9010 after annealing.jpg|right|thumb|Softening of Ag/Ni 90/10 after annealing for 1 hr after 80% cold working]]
[[File:Strain hardening of AgNi8020.jpg|right|thumb|Strain hardening of Ag/Ni 80/20 by cold working]]
[[File:Softening of AgNi8020 after annealing.jpg|right|thumb|Softening of Ag/Ni 80/20 after annealing for 1 hr after 80% cold working]]
[[File:Micro structure of AgNi9010.jpg|right|thumb|Micro structure of Ag/Ni 90/10 a) perpendicular to the extrusion direction b) parallel to the extrusion direction]]
[[File:Micro structure of AgNi 8020.jpg|right|thumb|Micro structure of Ag/Ni 80/20 a) perpendicular to the extrusion direction b) parallel to the extrusion direction]]
</figure>