Using copper as an alloying component increases the mechanical stability of silver significantly. The most important among the binary AgCu alloys is that of AgCu3, known in europe also under the name of hard-silver. This material still has a chemical corrosion resistance close to that of fine silver. In comparison to pure silver and fine-grain silver AgCu3 exhibits increased mechanical strength as well as higher arc erosion resistance and mechanical wear resistance ''<xr id="tab:tab2.14"/> (Table 2.14)''.
Increasing the Cu content further also increases the mechanical strength of AgCu alloys and improves arc erosion resistance and resistance against material transfer while at the same time however the tendency to oxide formation becomes detrimental. This causes during switching under arcing conditions an increase in contact resistance with rising numbers of operation. In special applications where highest mechanical strength is recommended and a reduced chemical resistance can be tolerated, the eutectic AgCu alloy with 28 wt% of copper ''(Fig. 2.52)'' is used. AgCu10 also known as coin silver has been replaced in many applications by composite silver-based materials while sterling silver (AgCu7.5) has never extended its important usage from decorative table wear and jewelry to industrial applications in electrical contacts.