<div class="multiple-images">
<figtable id="tab:tab2.2">
[[File:Physical Properties of Gold and Gold-Alloys.jpg|left|thumb| <caption>Tab 2.2 Physical Properties of Gold and Gold-Alloys</caption>]]
</figtable>
<figure id="fig:fig2.2">
[[File:Influence of 1-10 atomic of different.jpg|left|thumb|<caption>Fig 2.2 Influence of 1-10 atomic% of different alloying metals on the electrical resistivity of gold (according to J. O. Linde)</caption>]]
</figure>
</div>
<div class="multiple-images">
<figure id="fig:fig2.3">
[[File:Phase diagram of goldplatinum.jpg|left|thumb|<caption>Phase diagram of goldplatinum</caption>]]
</figure>
<figure id="fig:fig2.4">
[[File:Phase diagram of gold-silver.jpg|left|thumb|<caption>Phase diagram of gold-silver</caption>]]
</figure>
<figure id="fig:fig2.5">
[[File:Phase diagram of gold-copper.jpg|left|thumb|<caption>Phase diagram of gold-copper</caption>]]
</figure>
<figure id="fig:fig2.6">
[[File:Phase diagram of gold-nickel.jpg|left|thumb|<caption>Phase diagram of gold-nickel</caption>]]
</figure>
<figure id="fig:fig2.7">
[[File:Phase diagram of gold-cobalt.jpg|left|thumb|<caption>Phase diagram of gold-cobalt</caption>]]
</figure>
<figure id="fig:fig2.8">
[[File:Strain hardening of Au by cold working.jpg|left|thumb|<caption>Strain hardening of Au by cold working</caption>]]
</figure>
<figure id="fig:fig2.9">
[[File:Softening of Au after annealing for 0.5 hrs.jpg|left|thumb|<caption>Softening of Au after annealing for 0.5 hrs after 80% cold working</caption>]]
</figure>
<figure id="fig:fig2.10">
[[File:Strain hardening of AuPt10 by cold working.jpg|left|thumb|<caption>Strain hardening of AuPt10 by cold working</caption>]]
</figure>
<figure id="fig:fig2.11">
[[File:Strain hardening of AuAg20 by cold working.jpg|left|thumb|<caption>Strain hardening of AuAg20 by cold working</caption>]]
</figure>
<figure id="fig:fig2.12">
[[File:Strain hardening of AuAg30 by cold working.jpg|left|thumb|<caption>Strain hardening of AuAg30 by cold working</caption>]]
</figure>
<figure id="fig:fig2.13">
[[File:Strain hardening of AuNi5 by cold working.jpg|left|thumb|<caption>Strain hardening of AuNi5 by cold working</caption>]]
</figure>
<figure id="fig:fig2.14">
[[File:Softening of AuNi5 after annealing for 0.5 hrs.jpg|left|thumb|<caption>Softening of AuNi5 after annealing for 0.5 hrs after 80% cold working</caption>]]
</figure>
<figure id="fig:fig2.15">
[[File:Strain hardening of AuCo5 by cold working.jpg|left|thumb|<caption>Strain hardening of AuCo5 by cold working</caption>]]
</figure>
<figure id="fig:fig2.16">
[[File:Precipitation hardening of AuCo5 at.jpg|left|thumb|<caption>Precipitation hardening of AuCo5 at 400°C hardening temperature</caption>]]
</figure>
<figure id="fig:fig2.17">
[[File:Strain hardening of AuAg25Pt6 by cold working.jpg|left|thumb|<caption>Strain hardening of AuAg25Pt6 by cold working</caption>]]
</figure>
<figure id="fig:fig2.18">
[[File:Strain hardening of AuAg26Ni3 by cold working.jpg|left|thumb|<caption>Strain hardening of AuAg26Ni3 by cold working</caption>]]
</figure>
<figure id="fig:fig2.19">
[[File:Softening of AuAg26Ni3 after annealing for 0.5-hrs.jpg|left|thumb|<caption>Softening of AuAg26Ni3 after annealing for 0.5 hrs after 80% cold working</caption>]]
</figure>
<figure id="fig:fig2.20">
[[File:Strain hardening of AuAg25Cu5 by cold working.jpg|left|thumb|<caption>Strain hardening of AuAg25Cu5 by cold working</caption>]]
</figure>
<figure id="fig:fig2.21">
[[File:Strain hardening of AuAg20Cu10 by cold working.jpg|left|thumb|<caption>Strain hardening of AuAg20Cu10 by cold working</caption>]]
</figure>
<figure id="fig:fig2.22">
[[File:Softening of AuAg20Cu10 after annealing for 0.5 hrs.jpg|left|thumb|<caption>Softening of AuAg20Cu10 after annealing for 0.5 hrs after 80% cold working</caption>]]
</figure>
<figure id="fig:fig2.23">
[[File:Strain hardening of AuCu14Pt9Ag4 by cold working.jpg|left|thumb|<caption>Strain hardening of AuCu14Pt9Ag4 by cold working</caption>]]
</figure>
<figure id="fig:fig2.24">
[[File:Precipitation hardening of AuCu14Pt9Ag4.jpg|left|thumb|<caption>Precipitation hardening of AuCu14Pt9Ag4 at different hardening temperatures after 50% cold working</caption>]]
</figure>
</div>