Table 5.4: Mechanical Properties of Some Copper Types
<table border="1" cellspacing="0" style="border-collapse:collapse"><tr><td><p class="s3">Material</p></td><td><p class="s3">Condition</p></td><td><p class="s3">Tensile Strength</p><p class="s3">R<span class="s11">m</span></p><p class="s3">[MPa]</p></td><td><p class="s3">0,2% Yield</p><p class="s3">Strength R<span class="s11">p0,2</span></p><p class="s3">[MPa]</p></td><td><p class="s3">Elongation</p><p class="s3">A<span class="s11">50</span></p><p class="s3">[ %]</p></td><td><p class="s3">Hardness</p><p class="s3">HV</p></td></tr><tr><td><p class="s3">Cu-ETP Cu-OF Cu-HCP Cu-DLP Cu-DHP</p></td><td><p class="s3">R220</p></td><td><p class="s3">220 - 260</p></td><td><p class="s12"><1<span class="s3">40</span></p></td><td><p class="s12">>3<span class="s3">3</span></p></td><td><p class="s3">40 - 65</p></td></tr><tr><td><p class="s3">Cu-ETP Cu-OF Cu-HCP Cu-DLP Cu-DHP</p></td><td><p class="s3">R240</p></td><td><p class="s3">240 - 300</p></td><td><p class="s12">>1<span class="s3">80</span></p></td><td><p class="s12">>8</p></td><td><p class="s3">65 - 95</p></td></tr><tr><td><p class="s3">Cu-ETP Cu-OF Cu-HCP Cu-DLP Cu-DHP</p></td><td><p class="s3">R290</p></td><td><p class="s3">290 - 360</p></td><td><p class="s12">>2<span class="s3">50</span></p></td><td><p class="s12">>4</p></td><td><p class="s3">90 - 110</p></td></tr><tr><td><p class="s3">Cu-ETP Cu-OF Cu-HCP Cu-DLP Cu-DHP</p></td><td><p class="s3">R360</p></td><td><p class="s12">>3<span class="s3">60</span></p></td><td><p class="s12">>3<span class="s3">20</span></p></td><td><p class="s12">>2</p></td><td><p class="s12">>1<span class="s3">10</span></p></td></tr></table>
Fig. 5.1:
Strain hardening