Werkstoffe auf Silber-Basis

95 bytes added, 15:07, 20 March 2023
no edit summary
!Theoretische<br />Dichte<br />[g/cm<sup>3</sup>]
!Elektrische<br />Leitfähigkeit<br />[MS/m]
!Vickers<br />Härte<br />[HV0,1]
!Zugfestigkeit<br />[MPa]
!Dehnung (weichgeglüht)<br />A[%]min.
|10,4
|59 ± 2
|57 ± 15HV0,1
|215
|35
|10,1
|51 ± 2
|62 ± 15HV0,1
|255
|25
|9.9
|46 ± 5
|67 ± 15HV0,1
|270
|20
|10,1
|51 ± 2
|62 ± 15HV0,1
|255
|25
|9,8
|46 ± 5
|80 ± 10HV0,1
|
|
|9.8
|42 ± 5
|70 ± 10HV0,1
|
|
|9.8
|42 ± 5
|70 ± 10HV0,1
|
|
|10
|50 ± 2
|62 ± 15HV0,1
|240
|25
|10
|48 ± 2
|65 ± 15HV0,1
|240
|25
|9,8
|48 ± 2
|55 - 100HV0,1
|230 - 330
|28
|9,7
|46 ± 5
|60 - 106HV0,1
|235 - 330
|25
|9,9
|
|90 ± 10HV0,1
|
|
|9,8
|
|95 ± 10HV0,1
|
|
|9,8
|45 ± 5
|55 ± 10HV0,1
|
|
|9,9
|50 ± 5
|85 ± 15HV0,1
|310
|25
|9,8
|48 ± 5
|90 ± 15HV0,1
|325
|25
|9,6
|45 ± 5
|95 ± 15HV0,1
|330
|20