Fig. 2.41: Softening of PdCu15 after annealing for 0.5 hrs
 
 
<figure id="fig:Softening_of_PdCu15_after_annealing_for_0.5_hrs">
 
<figure id="fig:Softening_of_PdCu15_after_annealing_for_0.5_hrs">
 
[[File:Softening of PdCu15 after annealing.jpg|left|thumb|vSoftening of PdCu15 after annealing for 0.5 hrs</caption>]]
 
[[File:Softening of PdCu15 after annealing.jpg|left|thumb|vSoftening of PdCu15 after annealing for 0.5 hrs</caption>]]
 
</figure>
 
</figure>
  
 
Fig. 2.42: Strain hardening of PdCu40 by cold working
 
 
<figure id="fig:Strain_hardening_of_PdCu40_by_cold_working">
 
<figure id="fig:Strain_hardening_of_PdCu40_by_cold_working">
 
[[File:Strain hardening of PdCu40 by cold working.jpg|left|thumb|<caption>Strain hardening of PdCu40 by cold working</caption>]]
 
[[File:Strain hardening of PdCu40 by cold working.jpg|left|thumb|<caption>Strain hardening of PdCu40 by cold working</caption>]]
 
</figure>
 
</figure>
  
 
Fig. 2.43: Softening of PdCu40 after annealing for 0.5 hrs after 80% cold working
 
 
<figure id="fig:Softening_of_PdCu40_after_annealing_for_0.5_hrs_after_80%_cold_working">
 
<figure id="fig:Softening_of_PdCu40_after_annealing_for_0.5_hrs_after_80%_cold_working">
 
[[File:Softening of PdCu40 after annealing.jpg|left|thumb|<caption>Softening of PdCu40 after annealing for 0.5 hrs after 80% cold working</caption>]]
 
[[File:Softening of PdCu40 after annealing.jpg|left|thumb|<caption>Softening of PdCu40 after annealing for 0.5 hrs after 80% cold working</caption>]]
 
</figure>
 
</figure>
  
Fig. 2.44: Electrical resistivity p of PdCu alloys with and without an annealing step for forming an ordered phase
 
 
<figure id="fig:Electrical_resistivity_p_of_PdCu_alloys">
 
<figure id="fig:Electrical_resistivity_p_of_PdCu_alloys">
 
[[File:Electrical resistivity p of PdCu alloys.jpg|left|thumb|<caption>Electrical resistivity p of PdCu alloys with and without an annealing step for forming an ordered phase</caption>]]
 
[[File:Electrical resistivity p of PdCu alloys.jpg|left|thumb|<caption>Electrical resistivity p of PdCu alloys with and without an annealing step for forming an ordered phase</caption>]]

Revision as of 17:13, 13 February 2014

The platinum group metals include the elements Pt, Pd, Rh, Ru, Ir, and Os (Table 2.6). For electrical contacts platinum and palladium have practical significance as base alloy materials and ruthenium and iridium are used as alloying components. Pt and Pd have similar corrosion resistance as gold but because of their catalytical properties they tend to polymerize adsorbed organic vapors on contact surfaces. During frictional movement between contact surfaces the polymerized compounds known as “brown powder” are formed which can lead to significantly increase in contact resistance. Therefore Pt and Pd are typically used as alloys and not in their pure form for electrical contact applications.

Rhodium is not used as a solid contact material but is applied for example as a electroplated layer in sliding contact systems. Ruthenium is mostly used as an alloying component in the material PdRu15. The metals osmium and iridium have no practical applications in electrical contacts.

Since Pd was for the longest time rather stable in price it was looked at as a substitute for the more expensive gold. This was followed by a steep increase in the Pd price which caused a significant reduction in its use in electrical contacts. Today (2011) the Pd price again is lower than that of gold.

Alloys of Pt with Ru, Ir, Ni, and W were widely used in electromechanical components in the telecommunication industry and in heavy duty automotive breaker points (Table 2.7). Today these components have been replaced in many applications by solid state technology and the usage of these materials is greatly reduced. Pd alloys however have a more significant importance. PdCu15 is widely used for example in automotive flasher relays. Because of their resistance to sulfide formation PdAg alloys are applied in various relay designs. The ability to thermally precipitation harden some multi component alloys based on PdAgAuPt they find special usage in wear resistant sliding contact applications. Pd44Ag38Cu15PtAuZn is a standard alloy in this group.

Platinum and palladium alloys are mainly used similar to the gold based materials in the form of welded wire and profile segments but rarely as contact rivets. Because of the high precious metal prices joining technologies are used that allow the most economic application of the contact alloy in the area where functionally needed. Because of their resistance to material transfer they are used for DC applications and due to their higher arc erosion resistance they are applied for medium electrical loads up to about 30W in relays and switches (Table 2.10). Multi-component alloys based on Pd with higher hardness and wear resistance are mainly used as spring arms in sliding contact systems and DC miniature motors.

DEVELOP:ImageLIst

BEGIN=

Table 1 Properties, Production Processes, and Application Forms for Platinum Metals

Table 2

Physical Properties of the Platinum Metals and their Alloys

Table 3 Table 2.8: Mechanical Properties of the Platinum Metals and their Alloys

Figure 1 Fig. 2.25: Influence of 1-20 atom% of different additive metals on the electrical resistivity p of platinum (Degussa)

Figure 2 Fig. 2.26: Influence of 1-22 atom% of different additive metals on the electrical resistivity p of palladium

Figure 3 Fig. 2.27: Phase diagram of platinum-iridium

Figure 4 Fig. 2.28: Phase diagram of platinum-nickel

Figure 5 Fig. 2.29: Phase diagram of platinum-tungsten

Figure 6 Fig. 2.30: Phase diagram of palladium-copper

Figure 7 Fig. 2.31: Strain hardening of Pt by cold working

Figure 8 Fig. 2.32: Softening of Pt after annealing for 0.5 hrs after 80% cold working

Figure 9 Fig. 2.33: Strain hardening of PtIr5 by cold working

Figure 10 Fig. 2.34: Softening of PtIr5 after annealing for 1 hr after different degrees of cold working

Figure 11Fig. 2.35: Strain hardening of PtNi8 by cold working

Figure 12 Fig. 2.36: Softening of PtNi8 after annealing for 1 hr after 80% cold working

Figure 13Fig. 2.37: Strain hardening of PtW5 by cold working

Figure 14Fig. 2.38: Softening of PtW5 after annealing for 1hr after 80% cold working

Figure 15Fig. 2.39: Strain hardening of Pd 99.99 by cold working

Figure 16Fig. 2.40: Strain hardening of PdCu15 by cold working

Figure 17Fig. 2.41: Softening of PdCu15 after annealing for 0.5 hrs

Figure 18Fig. 2.42: Strain hardening of PdCu40 by cold working

Figure 19Fig. 2.43: Softening of PdCu40 after annealing for 0.5 hrs after 80% cold working

Figure 20Fig. 2.44: Electrical resistivity p of PdCu alloys with and without an annealing step for forming an ordered phase

Table 4Table 2.9: Contact and Switching Properties of the Platinum Metals and their Alloys

Table 5Table 2.10: Application Examples and Form of Supply for Platinum Metals and their Alloys

END=

PIsctures

Figure 1: Influence of 1- 20 atom% of different additive metals on the electrical resistivity p of platinum (Degussa)
Figure 2: Influence of 1-22 atom% of different additive metals on the electrical resistivity p of palladium


Figure 3: Fig. 2.27:Phase diagram of platinum-iridium


Figure 4: Fig. 2.28:Phase diagram of platinum-nickel
Figure 5: Fig. 2.29:Phase diagram of platinum-tungsten
Figure 6: Fig. 2.30: Phase diagram of palladium-copper
Figure 7: Fig. 2.31: Strain hardening of Pt by cold working
Figure 8: Fig. 2.32: Softening of Pt after annealing for 0.5 hrs after 80% cold working
Figure 9: Fig. 2.33: Strain hardening of PtIr5 by cold working
Figure 10: Fig. 2.34: Softening of PtIr5 after annealing for 1 hr after different degrees of cold working
Figure 11: Fig. 2.35: Strain hardening of PtNi8 by cold working
Figure 12: Fig. 2.36: Softening of PtNi8 after annealing for 1 hr after 80% cold working
Figure 13: Fig. 2.37: Strain hardening of PtW5 by cold working
Figure 14: Fig. 2.38: Softening of PtW5 after annealing for 1 hr after 80% cold working
Figure 15: Fig. 2.39: Strain hardening of Pd 99.99 by cold working
Figure 16: Fig. 2.40: Strain hardening of PdCu15 by cold working
vSoftening of PdCu15 after annealing for 0.5 hrs
Figure 18: Strain hardening of PdCu40 by cold working
Figure 19: Softening of PdCu40 after annealing for 0.5 hrs after 80% cold working
Figure 20: Electrical resistivity p of PdCu alloys with and without an annealing step for forming an ordered phase

=Tables

Table 1: Properties, Production Processes and Application Forms for Platinum Metals
Table 2.7: Physical Properties of the Platinum Metals and their Alloys


Table 3: Table 2.8 Mechanical Properties of the Platinum Metals and their Alloys

soft

70% cold worket

soft

70% cold

worket

soft

70% cold

worket

Pt (99,95)

150

360

40

3

40

120

PtIr5

260

550

25

2

85

160

PtIr10

340

570

24

2

105

210

PtRu10

650

1000

24

2

195

320

PtNi8

640

950

22

2

200

320

PtW5

530

860

21

2

150

270

Pd (99,95)

200

420

42

2

40

90

PdCu15

400

780

38

2

90

220

PdCu40

550

950

35

2

120

260

PdNi5

Pd35AuAgPt

340

700

25

2

95

200

420*

Pd44Ag38Cu15

405*

PtAuZn

Pd40Co40W20

680*

*maximum hardness

Table 2.9: Contact and Switching Properties of the Platinum Metals and their Alloys

Material

Properties

Pt

Very high corrosion resistance

PtIr5 - 10

Very high corrosion resistance, low contact resistance

High arc erosion resistance, high hardness

PtRu10

Very high corrosion resistance, low welding tendency

Low contact resistance, very

high hardness

PtNi8

Low material transfer tendency

Very high hardness

PtW5

Low material transfer tendency

High hardness

Pd

Strong tendency to “Brown Powder” formation

Less arc erosion resistant than Pt

PdCu15

PdCu40

Tendency to “Brown Powder” formation

Mostly resistant to material

transfer, high hardness

PdNi5

Strong tendency to “Brown Powder” formation

Low welding tendency

Pd44Ag38Cu15

PtAuZn

High mechanical wear resistance

Standard material for sliding

contact brushes


Table 2.10: Application Examples and Form of Supply for Platinum Metals and their Alloys

Material

Application Examples

Forms of Supply

Pt (99,95)

Relays

Contact rivets, welded contact parts

PtIr5

PtIr10

PtRu10

PtNi8

PtW5

Relays, sliding contact systems,

automotive ignition breaker points

Semi-finished Contact Materials:

Wire, seam-welded contact profiles

Contact Parts:

Tips, wire-formed parts, solid and composite contact rivets, welded contact parts

Pd (99,95)

PdNi5

Relays

Micro-profiles (weld tapes), contact rivets, welded contact parts

PdCu15

PdCu40

Automotive flasher relays

Micro-profiles, composite contact rivets

Pd35AuAgPt

Pd44Ag38Cu15

PtAuZn

Pd40Co40W20

Potentiometers, slip rings, miniature

DC motors

Wire-formed parts, welded wire segments, multi-arm sliding contact brushes