Switching Contacts

Switching Contacts

• Effects during switching operations

Figure 1: Contact opening with arc formation (schematic)

Influence of out-gasing from plastics


Figure 2: Histogram of the contact resistance R_K of an electroplated palladium layer (3 μm) with and without hard gold flash plating (0.2 μm) after exposure with different plastic materials

Figure 3: Contact resistance with exposure to out-gasing from plastics as a function of numbers of operations at 6 V_DC,100 mA: 1 Silicon containing plastic; 2 Plastics with strongly out-gasing components; 3 Plastics with minimal out-gasing components




• Influence of corrosive gases on the contact resistance





Figure 4: Distribution of cumulative frequency H of the contact resistance for solid contact rivets after 10 days exposure in a three-component test environment with 400 ppb each of H₂S, SO₂ and NO₂ at 25°C, 75% RH; Contact force 10cN; Measuring parameters: ≤ 40 mV_DC,10 mA; Probing contact: Gold rivet

Influences on contact areas in relays




• Contact Phenomena under the influence of arcing Matertia
• Material transfer

Figure 5: Material transfer under DC load a) Cathode; b) Anode.
Material: AgNi0.15; Switching parameters: 12V_DC, 3 A, 2x10⁶ perations
• Arc erosion

Figure 6: Arc erosion of a Ag/SnO₂ contact pair after extreme arcing conditions a) Overall view; b) Partial detail view
• Contact welding

Figure 7: Micro structure of a welded contact pair (Ag/SnO₂88/12 - Ag/CdO88/12) after extremely high current load. a) Ag/SnO₂88/12; b) Ag/CdO88/12