Fig. 2.25: Influence of 1-20 atom% of different additive metals on the electrical resistivity p of platinum (Degussa)
<xr id="fig:"Influence_of_1-20_atom%_of_different_additive_metals_on_the_electrical_resistivit_ p_of_platinum"/>
Fig. 2.26: Influence of 1-22 atom% of different additive metals on the electrical resistivity p of palladium
Fig. 2.27: Phase diagram of platinum-iridium
<xr id="fig:"Phase_diagram_of_platinum-nickel"/>
Fig. 2.28: Phase diagram of platinum-nickel
Fig. 2.29: Phase diagram of platinum-tungsten
<xr id="fig:"Phase_diagram_of_platinum-copper"/>
Fig. 2.30: Phase diagram of palladium-copper
<xr id="fig:"Strain_hardening_of_Pt_by_cold_working"/>
Fig. 2.31: Strain hardening of Pt by cold working
Fig. 2.32: Softening of Pt after annealing for 0.5 hrs after 80% cold working
<xr id="fig:Strain_hardening_of_PtIr5_by_cold_working"Strain_hardening_of_PtIr5_by_cold_working/>
Fig. 2.33: Strain hardening of PtIr5 by cold working
<xr id="fig:"Softening_of_PtIr5_after_annealing_for_1_hr_after_different_degrees_of_cold_working"/>
Fig. 2.34: Softening of PtIr5 after annealing for 1 hr after different degrees of cold working
<xr id="fig:"Strain_hardening_of_PtNi8_by_cold_working"/>Fig. 2.35: Strain hardening of PtNi8 by cold working
<xr id="fig:"Softening_of_PtNi8_after_annealing_for_1_hr_after_80%_cold_working"/>
Fig. 2.36: Softening of PtNi8 after annealing for 1 hr after 80% cold working
<xr id="fig:"Strain_hardening_of_PtW5_by_cold_working"/>Fig. 2.37: Strain hardening of PtW5 by cold working
<xr id="fig:"Softening_of_PtW5_after_annealing_for_1_hr_after_80%_cold_working"/>Fig. 2.38: Softening of PtW5 after annealing for 1hr after 80% cold working
<xr id="fig:"Strain_hardening_of_Pd_99.99_by_cold_working"/>Fig. 2.39: Strain hardening of Pd 99.99 by cold working
<xr id="fig:"Strain_hardening_of_PdCu15_by_cold_working"/>Fig. 2.40: Strain hardening of PdCu15 by cold working
<xr id="fig:"Softening_of_ PdCu15_after_annealing_for_0.5_hrs"/>Fig. 2.41: Softening of PdCu15 after annealing for 0.5 hrs
<xr id="fig:"Strain_hardening_of_PdCu40_by_cold_working"/>Fig. 2.42: Strain hardening of PdCu40 by cold working
<xr id="fig:"Softening_of_PdCu40_after_annealing_for_0.5_hrs_after_80%_cold_working"/>Fig. 2.43: Softening of PdCu40 after annealing for 0.5 hrs after 80% cold working
<xr id="fig:"Electrical_resistivity_p_of_PdCu_alloys"/>Fig. 2.44: Electrical resistivity p of PdCu alloys with and without an annealing step for forming an ordered phase
<xr id="fig:Contact_and_Switching_Properties_of_the_Platinum_Metals_and_their_Alloys"/>'''Table 2.9: Contact and Switching Properties of the Platinum Metals and their Alloys'''