Electroless Plating

From Electrical Contacts
Jump to: navigation, search

7.1.2.2 Immersion Processes

The immersion processes are usually applied in the plating of the metals gold, silver, and tin. If the material to be coated is less precious, i.e. exhibits a negative standard potential against the metal ions in the surrounding solution, it goes into solution releasing electrons while the more precious metal ions are reduced by absorbing electrons and being deposited on the electrode. This process can continue until the complete surface of the substrate is covered with a thin layer of the more precious metal. This limits the maximum achievable layer thickness to approx. 0.1 μm (Table 7.5).

Table 7.5: Immersion Gold Electrolytes

Type of Electrolyte

pH-Range

Coating Properties

Application Ranges

Type of Electrolyte

pH-Range

Hardness

HV 0.025

Punity

Application Ranges

Immersion Gold electrolytes

AUROL 4

AUROL 16

AUROL 20

3.8 - 4.2

5.8 - 6.2

5.8 - 6.2

5.8 - 6.2

60 - 80

60 - 80

60 - 80

60 - 80

99.99% Au

99.99% Au

99.99% Au

99.99% Au

Thin gold layers on Ni, Ni alloys,

Fe and Fe alloys for PCB technology and technical applications

7.1.2.3 Electroless Processes

The electroless metal plating with adding reduction agents to the electrolyte is based on the oxidation of the reducing agent with release of electrons which then in turn reduce the metal ions. To achieve a controlled deposition from such solutions the metal deposition has to happen through the catalytic influence of the substrate surface.

Otherwise a “wild” uncontrollable deposition would occur. In most cases palladium containing solutions are used for the activation which seed the surfaces with palladium and act as catalysts in the copper and nickel electrolytes.

The electrolytes contain besides the complex ion compounds of the metals to be deposited also stabilizers, buffer and accelerator chemicals, and a suitable reduction agent.

These electrolytes are usually operating at elevated temperatures (50° – 90°C). The deposits contain besides the metals also process related foreign inclusions such as for example decomposition products of the reduction agents. The electroless processes are used mainly for copper, nickel, and gold deposits.

7.1.2.4 Electroless Deposition of Nickel/Gold

Electroless deposited nickel coatings with an additional immersion layer of gold are seeing increased importance in the coating of printed circuit boards (PCBs). The process sequence is shown in (Fig. 7.2) using the example of the DODUCHEM process.

Tabelle

After the pre-cleaning (degreasing and etching) a palladium sulfate activator is used which activates the exposed copper surfaces on the printed circuit board and thus facilitates the nickel deposition. The electroless working chemical nickel electrolyte contains – besides other ingredients – Sodium-hypophosphite, which is reduced to phosphorus in a parallel occurring process and incorporated into the nickel deposit. At the temperature of 87 – 89°C a very homogeneous nickel-phosphorus alloy layer with approx. 9 wt% P is deposited with layer thicknesses > 5 μm possible. During a consecutive processing step a very thin and uniform layer (< 0.1 μm) of gold is added in an immersion electrolyte. This protects the electroless nickel layer against corrosion achieving a solderable and well bondable surface for thick or fine aluminum bond wires.

It is possible to enhance this layer combination further by adding a immersion palladium layer between the electroless nickel and the gold coating (DODUBOND process). This Pd layer acts as a diffusion barrier and allows the usage of this surface combination also for gold wire bonding.

As an alternative, for gold wire bonding applications a thicker gold layer of 0.2 – 0.5 μm can be applied using an electroless process. Typical electrolytes work at a temperature of approx. 80°C with deposition rates of 0.3 – 0.4 μm per 30 minutes. There are however limitations with these electroless electrolytes concerning their stability and the robustness of the process compared to other electroplating processes which reduces their wider usage (Fig. 7.3).

Fig. 7.3: Coating composition of a printed circuit board with reductively enhanced gold

7.1.2.5 Immersion Deposition of Tin

A tin coating by ion exchange is usually not possible since copper is the more precious metal. By adding thio-urea the electro-chemical potential of copper is reduced to a level (approx. 450 mV, significantly lower than tin) that allows the exchange reaction. Using a suitable electrolyte composition and enhancer solutions like with the DODUSTAN process (Fig. 7.4) tin coatings can be produced that, even under usually unfavorable conditions of copper concentrations of 7 g/l in the electrolyte, are well solderable.

Fig. 7.4: Process flow for electroless tin deposition using the DODUSTAN process

The immersion tin deposition is suitable for the production of a well solderable surface on printed circuit boards and electronic components. It is also used as an etch resist against ammonia based solutions or as corrosion and oxidation protection of copper surfaces.