<caption>'''<!--Table 8.1:-->verschiedene Typen von Silber-Pulvern'''</caption>
<table class="twocolortable">
<tr><th><p class="s6">Powder typePulvertyp</p></th><th><p class="s6">GE</p></th><th><p class="s6">GN1</p></th><th><p class="s7">ES</p></th><th><p class="s6">V</p></th></tr><tr><td><p class="s6">Manufacturing Herstellung Process</p></td><td><p class="s6">chemicalchem.</p></td><td><p class="s6">chemicalchem.</p></td><td><p class="s7">electrolyticelektrolytisch</p></td><td><p class="s6">atomizedverdüst</p></td></tr><tr><td><p class="s6">Particle shapeKornform</p></td><td><p class="s6">agglomeratedagglomeriert</p></td><td><p class="s6">agglomeratedagglomeriert</p></td><td><p class="s7">dentriticdendritisch</p></td><td><p class="s6">sphericalkugelig</p></td></tr><tr><td><p class="s6">AvgMittl. particle diameterKorndurchmesser</p><p class="s6">(median) [µm]</p></td><td><p class="s6">10 - 15</p></td><td><p class="s6">20 - 40</p></td><td><p class="s7">-</p></td><td><p class="s6">32 - 60</p></td></tr><tr><td><p class="s6">Medium particle sizeMittl. Korndurchmesser</p><p class="s6">(FSS - Fisher Sub Sieve Size) [µm]</p></td><td><p class="s6">-</p></td><td><p class="s6">-</p></td><td><p class="s7">4.0 - 6.0</p></td><td><p class="s6">-</p></td></tr><tr><td><p class="s6">Tap densityKlopfdichte nach </p><p class="s6">(DIN/ISO 3953) [g/cm<sup>3</sup>]</p></td><td><p class="s6">0.7 - 1.1</p></td><td><p class="s6">2.0 - 2.5</p></td><td><p class="s7">2.0 - 3.0</p></td><td><p class="s6">4.0 - 6.7</p></td></tr><tr><td><p class="s6">Specific surface areaSpez. Oberfläche </p><p class="s6">(nach B.E.T.) [m<sup>2</sup>/g]</p></td><td><p class="s6">0.5 - 0.9</p></td><td><p class="s6">-</p></td><td><p class="s7">-</p></td><td><p class="s6">-</p></td></tr></table>
</figtable>
<caption>'''<!--Table 8.2:-->Flüssige Silber-Präparate zum Einbrennen (ARGONOR)'''</caption>
<table class="twocolortable" style="width:80%">
<tr><th><p class="s6">PreparationPräparat</p></th><th><p class="s6">Substrate</p><p class="s6">Material</p></th><th><p class="s6">Application byVerarbeitung</p></th><th><p class="s6">Firing Temperature Einbrenntemperatur [°C]</p></th><th><p class="s6">PropertiesEigenschaften</p></th><th><p class="s6">Silver Content Silbergehalt<br />[wtMassen-%]</p></th></tr><tr><td><p class="s6">Argonor N92</p></td><td><p class="s6">glassGlas, ceramicsKeramik</p></td><td><p class="s6">paint brush, spray gunPinsel Spritzpistole</p></td><td><p class="s6">530 - 650</p></td><td><p class="s6">ViscosityViskosität</p><p class="s6">500 – 1.000 mPa·s, good solderabilitygute Lötbarkeit</p></td><td><p class="s6">65</p></td></tr><tr><td><p class="s6">Argonor</p></td><td><p class="s6">glassGlas,</p><p class="s6">ceramicsKeramik</p></td><td><p class="s6">screen</p><p class="s6">printingSiebdruck</p></td><td><p class="s6">530 - 650</p></td><td><p class="s6">ViscosityViskosität</p><p class="s6">10 – 15.000 mPa·s, good solderabilitygute Lötbarkeit</p></td><td><p class="s6">65</p></td></tr></table>
</figtable>
{| class="twocolortable" style="text-align: left; font-size: 12px"
|-
!Preparation Präparat !Substrate<br />MaterialTrägermaterial!Application byVerarbeitung!DryingTrocknung<br />[°C]!PropertiesEigenschaften!Usage AmountVerbrauch<br />[g/100 cm<sup>2</sup>]!Area ResistanceFlächenwiderstand<br />[Ω/m<sup>2</sup>]
|-
|AROMAL 38
|glassGlas, plasticsKunststoff|sprayingSpritzen, immersionTauchen,<br />paint brushPinsel
|RT,<br />30 min<br />100°C
|hard well conductingHarte, gut leitende Silberschicht<br />Ag layer for broad applicationsmit breitem Einsatzgebiet
|0.5 - 2
|< 0.1
|-
|AROMAL 50
|glassGlas, waxWachs, plasticsKunststoff|sprayingSpritzen, immersionTauchen,<br />paint brushPinsel
|10 min<br />RT
|very flat surfaceSehr ebene Oberfläche,besonders<br />especially for electrolytic build-upzum galvanischen Verstärken
|0.5 - 2
|< 0.2
|-
|AROMAL 70T
|plasticsKunststoff|tampon printingTampondruck
|60 min<br />RT
|hard and well conductive coatingHarte, gut leitende Beschichtung
|
|< 0.1
|-
|AROMAL 141
|plasticsKunststoff,<br />paper- based plasticsHartpapier|screen printingSiebdruck
|45 min<br />120°C
|mechanically Mechanisch<br />very strong coatingssehr feste Überzüge
|
|< 0.05
|-
|AROMAL 170
|plasticsKunststoff|screen printingSiebdruck
|30 min<br />100°C
|flexible layersFlexible Schichten,besonders<br />well suited for foil materialsfür Folien geeignet
|
|< 0.05
|AROMAL K 5 A+B
|metal, glass
|dispenserDispenser,<br />screen printingSiebdruck
|24h RT,<br />3h<br />80°C
|mechanically very strongMechanisch sehr feste Verbindungen<br />bond connection<br />as alternative to solderingals Alternative zum Weichlöten
|
|< 0.1
|-
|AROMAL K 20
|metalMetall, plasticsKunststoff,<br />ceramicsKeramik|dispenserDispenser,<br />screen printingSiebdruck
|15 min<br />150°C
|flexible bonds which helpFlexible Verbindungen, die<br />decrease thermal stressesthermische Spannungen abbauen helfen
|
|< 0.1
|-
|DOSILAC
|colspan="6" |Silver conductive paints Silber-Leitlack in spray cansSpraydose abgefüllt; can be spray painted; properties similar to those of als Spühlack verwendbar, mit ähnlichen Eigenschaften wie AUROMAL 50
|}
</figtable>
===Edelmetall-Flakes===
<figure id="fig:SEM photos of silver flakes a fine grain b large flat">
[[File:SEM photos of silver flakes a fine grain b large flat.jpg|right|thumb|REM-Aufnahmen von Silber-Flakes SEM photos of silver flakes (a) feinkörnig fine grain (b) großflächiglarge flat]]
</figure>
{| class="twocolortable" style="text-align: left; font-size: 12px;width:80%"
|-
!Type of Flake-Typ
!F56
!B190
!ES4
|-
|Main characteristicsCharakteristische Merkmale|Low tap densitygeringe Klopfdichte|Very finesehr fein|Purerein, wide grain size distributionbreite Kornverteilung
|-
|Silver content Silbergehalt [wtMassen-%]
|> 99.0
|> 99.0
|> 99.7
|-
|MedMittl. Grain size Korndurchmesser (50%-Median) [μm] Tap density
|3 - 8
|4 - 6
|9 - 13
|-
|Klopfdichte nach DIN/ISO 3953 [g/cm<sup>3</sup>cm³]
|0.7 - 1.1
|2.1 - 2.7
|2.7 - 3.6
|-
|SpecSpez. Surface area Oberfläche nach B.E.T. [m<sup>2</sup>m²/g]
|0.7 - 1.1
|0.3 - 0.7