Brazing Alloys and Fluxes

Revision as of 16:43, 26 November 2013 by Kpeters (talk | contribs)


Contents

4.1 Brazing Alloys

For the joining of contact materials with carrier substrates brazing alloys with working temperatures > 600 °C are used exclusively. The working temperature is defined as the lowest surface temperature by which the brazing material wets the materials to be joined. This temperature is within the melting range and between the solidus (temperature at which melting starts) and liquidus (temperature at complete liquid state) point of the brazing alloy. Silver-based brazing alloys have good electrical conductivity and a sufficient mechanical strength which allows a bonding process without significant changes in the 4 microstructure of the material to be joined. For electrical contacts usually low-melting alloys with a minimum of 20 wt-% silver and additions of cadmium, zinc or tin to lower the melting point are used (Table 4.1). Because of the toxicity of cadmium most cadmium containing brazing alloys have been replaced by zinc and tin containing brazing alloys. For higher requirements on corrosion resistance or for easier wetting of stainless steel nickel and manganese containing alloys are also used. Using any of these brazing alloys in an air environment is only possible with the addition of oxide reducing fluxes. For high temperature brazing in vacuum or protective atmosphere vacuum melted silver-copper eutectic brazing alloys are used. These also allow subsequent forming operations due to their higher ductility. For the brazing of contacts with a silver bottom layer to copper backings phosphorous containing brazing alloys which eliminate the need for a flux application are widely used. The brazing alloy is typically introduced into the joint area in the form of wire segments, foil, shims, or as powder or paste. For larger production volumes it is economically advantageous to pre-coat contact tips with a thin layer (< 100 µm) of brazing alloy.

4.2 Fluxes

Brazing fluxes consist of non-metallic materials, mostly salt mixtures of boron and halogen compounds (Table 4.2). Their purpose is to remove oxides from the brazing surfaces and prevent their new build-up in order to allow a thorough wetting of these surfaces by the liquefied brazing alloy. Fluxes have to be activated already at a temperature below the working range of the brazing alloy. They are selected mainly according to the working temperature of the brazing alloy and the base material to be joined.

Table 4.1: Commonly Used Brazing Alloys for Electrical Contacts
Designation Designation Designation Composition Melting range Working Electrical

Conductivity

Density Application
DIN EN 1044 US (equivalent or closest

similar brazing alloy)

DIN EN ISO 3677 wt% Temperature

[°C]

[MS/m] [g/m³]
AG 304*) BAg-1 B-Ag40ZnCdCu-

595/630

Ag39 - 41

Cd18 - 22 Cu18 - 20 Zn19 - 23

595 630 610 14.0 9.3 Cu,Cu alloys,

Ag materials, Fe, Ni

AG 306*) BAg-2a B-Ag30CuCdZn-

600/765

Ag30 - 32

Cu28 - 30 Cd21 - 25 Zn21 - 25

600 690 680 13.0 9.2 Cu, Cu alloys,

Ag materials, Fe, Ni

Since the residues of fluxes are hygroscopic and can cause corrosion they have to be removed completely after the brazing process in very hot or boiling water. Depending on the type and process used, fluxes are being applied in liquid form or as powders or pastes.

4.2 Fluxes for the Brazing of Heavy Metals
Designation

DIN EN 1045

Designation US (similar) Active temperature range [°C] Chemical ingredients Base materials used for
TYP FH 10 FB 3-A 550 - 800 Boron compounds, Fluorides All metals and alloys except light metals,

alloyed steels, carbide steel

TYP FH 11 FB 4-A 550 - 800 Boron compounds,

Fluorides, Chlorides

Copper,

Aluminum bronze

TYP FH 12 FB 3-C 550 - 850 Boron,

Boron compounds, Fluorides

Special brass,

any steel alloys, carbide steel

TYP FH 21 FB 3-I 750 - 1100 Boron compounds, Chlorides All metals and alloys

except light metals