Werkstoffe auf Silber-Basis - Revision history

Doduco Admin at 08:26, 8 September 2025

2025-09-08T08:26:48Z

Doduco Admin at 14:12, 20 August 2025

2025-08-20T14:12:10Z

Doduco Admin at 12:46, 9 May 2025

2025-05-09T12:46:04Z

Doduco Admin at 12:05, 27 March 2023

2023-03-27T12:05:07Z

Doduco Admin at 12:01, 27 March 2023

2023-03-27T12:01:40Z

Doduco Admin at 14:07, 20 March 2023

2023-03-20T14:07:51Z

Doduco Admin at 14:01, 20 March 2023

2023-03-20T14:01:19Z

Doduco Admin at 09:17, 2 March 2023

2023-03-02T09:17:08Z

Doduco Admin: /* Silber-Metalloxid-Werkstoffe Ag/CdO, Ag/SnO2, Ag/ZnO */

2023-02-17T07:15:11Z

‎Silber-Metalloxid-Werkstoffe Ag/CdO, Ag/SnO2, Ag/ZnO

Show changes

Doduco Admin at 07:28, 26 January 2023

2023-01-26T07:28:11Z

@@ Line 1,808: / Line 1,808: @@
 !Spez. elektr. Widerstand (20°)<br />[μΩ·cm]
 !colspan="2" style="text-align:center"|Elektrische Leitfähigkeit<br />[% IACS]  [MS/m]
-!Vickershärte<br />HV10<br />42 - 45
+!Vickershärte<br />HV10
 |-
 |Ag/C 98/2<br />
@@ Line 1,817: / Line 1,817: @@
 |90 - 93
 |48 - 50
-|42 - 44
+|42 - 45
 |-
 |Ag/C 97/3<br />
@@ Line 1,826: / Line 1,826: @@
 |86 - 90
 |45 - 48
-|41 - 43
+|42 - 44
 |-
 |Ag/C 96/4<br />
@@ Line 1,835: / Line 1,835: @@
 |81 - 84
 |42 - 46
-|40 - 42
+|41 - 43
 |-
 |Ag/C 95/5<br />
@@ Line 1,844: / Line 1,844: @@
 |78 - 81
 |40 - 44
-|40 - 60
+|40 - 42
 |-
 |AgC DF*)
@@ Line 1,853: / Line 1,853: @@
 |69 - 76
 |40 - 44
+|40 - 60
 |}
 </figtable>

@@ Line 1,846: / Line 1,846: @@
 |40 - 60
 |-
-|AgC DF<br />GRAPHOR DF*)
+|AgC DF*)
 |95.7 - 96.7
 |8.7 - 8.9

@@ Line 972: / Line 972: @@
 Umformgrad beim Strangpressen wird eine gleichmäßige Verteilung der
 CdO-Partikel in der Ag-Matrix und eine hohe Dichte erreicht, die sich vorteilhaft
-auf die Kontakteigenschaften auswirken (<xr id="fig:Micro structure of AgCdO9010P"/><!--(Fig. 2.84)-->). Die für Bänder und Plättchen
+auf die Kontakteigenschaften auswirken (<xr id="fig:Micro structure of AgCdO9010"/><!--(Fig. 2.84)-->). Die für Bänder und Plättchen
 erforderliche gut löt- und schweißbare Unterseite wird durch Verbundstrangpressen
 oder Anplattieren einer Silberschicht nach oder vor dem
@@ Line 1,023: / Line 1,023: @@
 <figure id="fig:Micro structure of AgCdO9010P">
-[[File:Micro structure of AgCdO9010P.jpg|left|thumb|<caption>Gefüge von Ag/CdO 90/10 P a) senkrecht zur Strangpressrichtung
+[[File:Micro structure of AgCdO9010P.jpg|left|thumb|<caption>Gefüge von Ag/CdO 90/10  a) senkrecht zur Strangpressrichtung
 b) parallel zur Strangpressrichtung</caption>]]
 </figure>

@@ Line 334: / Line 334: @@
 ====Feinkornsilber====
-Unter Feinkornsilber (ARGODUR-Spezial) versteht man eine Silberlegierung mit
+Unter Feinkornsilber versteht man eine Silberlegierung mit
 einem Zusatz von 0,15 Massen-% Nickel. Silber und Nickel sind im festen Zustand
 ineinander völlig unlöslich. Im flüssigen Silber lässt sich nur ein geringer
@@ Line 541: / Line 541: @@
 |'''Halbzeuge:'''<br />Bänder, Drähte, Kontaktprofile, Kontaktbimetalle, rollennahtgeschweißte Profile<br />'''Kontaktteile:'''<br />Kontaktauflagen, massive Kontaktniete, Aufschweißkontakte, plattierte, geschweißte und genietete Kontaktteile
 |-
-|Ag99, 5NiOMgO<br />ARGODUR 32
+|Ag99,5NiOMgO<br />ARGODUR 32
 |Miniaturrelais, Schütze und Relais in Flugzeugen, Erodierdrähte für Einspritzdüsen
 |Kontaktfedern, Kontaktträgerteile
@@ Line 1,506: / Line 1,506: @@
 !Lieferform
 |-
-|Ag/ZnO 92/8P<br />
+|Ag/ZnO 92/8SP<br />
 |91 - 93
+|
@@ Line 1,548: / Line 1,548: @@
 |1
 |-
-|Ag/ZnO 92/8WP<br />
+|Ag/ZnO 92/8SP<br />
 |91 - 93
+|

@@ Line 1,081: / Line 1,081: @@
 !Art der Bereitstellung
 |-
-|Ag/SnO<sub>2</sub> 98/2 SPW10
+|Ag/SnO<sub>2</sub> 98/2 SPW
 |97 - 99
 |WO<sub>3</sub>

@@ Line 1,075: / Line 1,075: @@
 !Theoretische<br />Dichte<br />[g/cm<sup>3</sup>]
 !Elektrische<br />Leitfähigkeit<br />[MS/m]
-!Vickers<br />Härte<br />[HV0,1]
+!Vickers<br />Härte<br />
 !Zugfestigkeit<br />[MPa]
 !Dehnung (weichgeglüht)<br />A[%]min.
@@ Line 1,086: / Line 1,086: @@
 |10,4
 |59 ± 2
-|57 ± 15
+|57 ± 15 HV0,1
 |215
 |35
@@ Line 1,097: / Line 1,097: @@
 |10,1
 |51 ± 2
-|62 ± 15
+|62 ± 15 HV0,1
 |255
 |25
@@ Line 1,119: / Line 1,119: @@
 |9.9
 |46 ± 5
-|67 ± 15
+|67 ± 15 HV0,1
 |270
 |20
@@ Line 1,130: / Line 1,130: @@
 |10,1
 |51 ± 2
-|62 ± 15
+|62 ± 15 HV0,1
 |255
 |25
@@ Line 1,152: / Line 1,152: @@
 |9,8
 |46 ± 5
-|80 ± 10
+|80 ± 10 HV0,1
+|
+|
@@ Line 1,163: / Line 1,163: @@
 |9.8
 |42 ± 5
-|70 ± 10
+|70 ± 10 HV0,1
+|
+|
@@ Line 1,196: / Line 1,196: @@
 |9.8
 |42 ± 5
-|70 ± 10
+|70 ± 10 HV0,1
+|
+|
@@ Line 1,240: / Line 1,240: @@
 |10
 |50 ± 2
-|62 ± 15
+|62 ± 15 HV0,1
 |240
 |25
@@ Line 1,251: / Line 1,251: @@
 |10
 |48 ± 2
-|65 ± 15
+|65 ± 15 HV0,1
 |240
 |25
@@ Line 1,273: / Line 1,273: @@
 |9,8
 |48 ± 2
-|55 - 100
+|55 - 100 HV0,1
 |230 - 330
 |28
@@ Line 1,284: / Line 1,284: @@
 |9,7
 |46 ± 5
-|60 - 106
+|60 - 106 HV0,1
 |235 - 330
 |25
@@ Line 1,295: / Line 1,295: @@
 |9,9
+|
-|90 ± 10
+|90 ± 10 HV0,1
+|
+|
@@ Line 1,306: / Line 1,306: @@
 |9,8
+|
-|95 ± 10
+|95 ± 10 HV0,1
+|
+|
@@ Line 1,317: / Line 1,317: @@
 |9,8
 |45 ± 5
-|55 ± 10
+|55 ± 10 HV0,1
+|
+|
@@ Line 1,328: / Line 1,328: @@
 |9,9
 |50 ± 5
-|85 ± 15
+|85 ± 15 HV0,1
 |310
 |25
@@ Line 1,339: / Line 1,339: @@
 |9,8
 |48 ± 5
-|90 ± 15
+|90 ± 15 HV0,1
 |325
 |25
@@ Line 1,350: / Line 1,350: @@
 |9,6
 |45 ± 5
-|95 ± 15
+|95 ± 15 HV0,1
 |330
 |20

@@ Line 1,141: / Line 1,141: @@
 |10
+|
+|68 ± 15 HV5
+|
+|
@@ Line 1,174: / Line 1,174: @@
+|
+|
+|60 ± 15 HV5
+|
+|
@@ Line 1,207: / Line 1,207: @@
 |10,4
 |57 ± 2
+|45 ± 15 HV5
 |215
 |35
@@ Line 1,227: / Line 1,227: @@
 |93 - 95
 |Bi<sub>2</sub>O<sub>3</sub> und CuO
+|10,0
+|53 ± 2
+|58 ± 15 HV0,1
+|230
+|30
 |Pulvermetallurgisch
 |1,2
@@ Line 1,262: / Line 1,262: @@
 |9,9
 |46 ± 5
+|75 ± 15 HV5
 |260
 |20

@@ Line 1,334: / Line 1,334: @@
 |1,2
 |-
-|Ag/SnO<sub>2</sub> 90/10 POX1
+|Ag/SnO<sub>2</sub> 88/12 POX1
 |87 - 89
 |In<sub>2</sub>O<sub>3</sub>
@@ Line 1,345: / Line 1,345: @@
 |1,2
 |-
-|Ag/SnO<sub>2</sub> 90/10 POX1
+|Ag/SnO<sub>2</sub> 86/14 POX1
 |85 - 87
 |In<sub>2</sub>O<sub>3</sub>

@@ Line 513: / Line 513: @@
 !colspan="2" | Eigenschaften
 |-
-|Ag<br />AgNi0,15<br />ARGODUR-Special
+|Ag<br />AgNi0,15<br />
 |Höchste elektrische und thermische Leitfähigkeit, hohe Affinität zu Schwefel (Sulfidbildung), geringe Verschweißresistenz, niedriger Kontaktwiderstand, sehr gute Verformbarkeit
 |oxidationsbeständig, bei höheren Einschaltströmen begrenzte Abbrandfestigkeit, Neigung zur Materialwanderung in Gleichstromkreisen, gute Löt- und Schweißbarkeit
@@ Line 533: / Line 533: @@
 !Lieferformen
 |-
-|Ag<br />AgNi0,15<br />ARGODUR-Spezial<br />AgCu3<br />AgNi98NiCu2<br />ARGODUR 27<br />AgCu24,5Ni0,5
+|Ag<br />AgNi0,15<br /><br />AgCu3<br />AgNi98NiCu2<br />ARGODUR 27<br />AgCu24,5Ni0,5
 |Relais,<br />Mikroschalter,<br />Hilfsstromschalter,<br />Befehlsschalter,<br />Schalter für Hausgeräte,<br />Lichtschalter (&le; 20A),<br />Hauptschalter
 |'''Halbzeuge:''' <br />Bänder, Drähte, Kontaktprofile, Kontaktbimetalle, Toplay-Profile, rollennahtgeschweißte Profile<br />'''Kontaktteile:'''<br />Kontaktauflagen, massive- und Bimetallniete, Aufschweißkontakte, plattierte, geschweißte und genietete Kontaktteile