====Picture====
<xr id="fig:fig2.52"/> Fig. 2.52: Phase diagram of silver-copper
<xr id="fig:fig2.53"/> Fig. 2.53: Phase diagram of silver-cadmium
<xr id="fig:fig2.54"/> Fig. 2.54: Strain hardening of AgCu3 by cold working
<xr id="fig:fig2.55"/> Fig. 2.55: Softening of AgCu3 after annealing for 1 hr after 80% cold working
<xr id="fig:fig2.56"/> Fig. 2.56: Strain hardening of AgCu5 by cold working
<xr id="fig:fig2.57"/> Fig. 2.57: Softening of AgCu5 after annealing for 1 hr after 80% cold working
<xr id="fig:fig2.58"/> Fig. 2.58: Strain hardening of AgCu 10 by cold working
<xr id="fig:fig2.59"/> Fig. 2.59: Softening of AgCu10 after annealing for 1 hr after 80% cold working
<xr id="fig:fig2.60"/> Fig. 2.60: Strain hardening of AgCu28 by cold working
<xr id="fig:fig2.61"/> Fig. 2.61: Softening of AgCu28 after annealing for 1 hr after 80% cold working
<xr id="fig:fig2.62"/> Fig. 2.62: Strain hardening of AgNi0.15 by cold working
<xr id="fig:fig2.63"/> Fig. 2.63: Softening of AgNi0.15 after annealing for 1 hr after 80% cold working
<xr id="fig:fig2.64"/> Fig. 2.64: Strain hardening of ARGODUR 27 by cold working
<xr id="fig:fig2.65"/> Fig. 2.65: Softening of ARGODUR 27 after annealing for 1 hr after 80% cold working
<div class="multiple-images">
<figure id="fig:fig2.52"> Fig. 2.52: Phase diagram of silver-copper
</figure>
<figure id="fig:fig2.53"> Fig. 2.53: Phase diagram of silver-cadmium
[[File:Phase diagram of silver cadmium.jpg|right|thumb|Phase diagram of silver-cadmium]]
</figure> <figure id="fig:fig2.54"> Fig. 2.54: Strain hardening of AgCu3 by cold working
[[File:Strain hardening of AgCu3 by cold working.jpg|right|thumb|Strain hardening of AgCu3 by cold working]]
</figure>
<figure id="fig:fig2.55"> Fig. 2.55: Softening of AgCu3 after annealing for 1 hr after 80% cold working
[[File:Softening of AgCu3 after annealing.jpg|right|thumb|Softening of AgCu3 after annealing for 1 hr after 80% cold working]]
</figure> <figure id="fig:fig2.56"> Fig. 2.56: Strain hardening of AgCu5 by cold working
[[File:Strain hardening of AgCu5 by cold working.jpg|right|thumb|Strain hardening of AgCu5 by cold working]]
</figure> <figure id="fig:fig2.57"> Fig. 2.57: Softening of AgCu5 after annealing for 1 hr after 80% cold working
[[File:Softening of AgCu5 after annealing.jpg|right|thumb|Softening of AgCu5 after annealing for 1 hr after 80% cold working]]
</figure> <figure id="fig:fig2.58"> Fig. 2.58: Strain hardening of AgCu 10 by cold working
[[File:Strain hardening of AgCu 10 by cold working.jpg|right|thumb|Strain hardening of AgCu 10 by cold working]]
</figure> <figure id="fig:fig2.59"> Fig. 2.59: Softening of AgCu10 after annealing for 1 hr after 80% cold working
[[File:Softening of AgCu10 after annealing.jpg|right|thumb|Softening of AgCu10 after annealing for 1 hr after 80% cold working]]
</figure> <figure id="fig:fig2.60"> Fig. 2.60: Strain hardening of AgCu28 by cold working
[[File:Strain hardening of AgCu28 by cold working.jpg|right|thumb|Strain hardening of AgCu28 by cold working]]
</figure> <figure id="fig:fig2.61"> Fig. 2.61: Softening of AgCu28 after annealing for 1 hr after 80% cold working
[[File:Softening of AgCu28 after annealing.jpg|right|thumb|Softening of AgCu28 after annealing for 1 hr after 80% cold working]]
</figure> <figure id="fig:fig2.62"> Fig. 2.62: Strain hardening of AgNi0.15 by cold working
[[File:Strain hardening of AgNiO15 by cold working.jpg|right|thumb|Strain hardening of AgNiO15 by cold working]]
</figure> <figure id="fig:fig2.63"> Fig. 2.63: Softening of AgNi0.15 after annealing for 1 hr after 80% cold working
[[File:Softening of AgNiO15 after annealing.jpg|right|thumb|Softening of AgNiO15 after annealing]]
</figure> <figure id="fig:fig2.64"> Fig. 2.64: Strain hardening of ARGODUR 27 by cold working
[[File:Strain hardening of ARGODUR 27.jpg|right|thumb|Strain hardening of ARGODUR 27 by cold working]]
</figure> <figure id="fig:fig2.65"> Fig. 2.65: Softening of ARGODUR 27 after annealing for 1 hr after 80% cold working
[[File:Softening of ARGODUR 27 after annealing.jpg|right|thumb|Softening of ARGODUR 27 after annealing for 1 hr after 80% cold working]]
</figure>
</div>
<div class="clear"></div>
'''Table 2.15: Contact and Switching Properties of Silver and Silver Alloys'''